测量了使用溶胶-凝胶工艺制备的 (Bi0.5Na0.5)1- xBaxTiO3(x=0,0.02,0.04,0.06)系无铅 压电陶瓷的介电、压电和弹性参数.研究发现,该工艺制备的 (Bi0.5Na0.5)0.94Ba0.06TiO3陶瓷具有 此系列最强的压电性能, 与传统工艺制备的该类压电陶瓷相比, 溶胶-凝胶工艺制备的 (Bi0.5Na0.5)0.94Ba0.06TiO3陶瓷具有压电常数( d33=173× 10- 12C/N)、机电耦合系数( kt=56%, kp= 26%)、泊松比(ν =0.3)提高; 频率常数( Nt=2250Hz· m, Np=2810Hz· m)、退极化温度( Td= 75℃)降低以及介电常数(εTr33=820)、介电损耗( tgδ=3.9%)稍大的特点.

参考文献

[1] Takenaka T;Maruyama K;Sakata K .(Bi0.5Na0.5)TiO3- BaTiO3 System for Lead- Free Piezoelectric Ceramics[J].Japanese Journal of Applied Physics,1991,30:2236-2239.
[2] Atsushi Sasaki;Tatsuya Chiba;Youichi Mamiya;Etsuo Otsuki .Dielectric and Piezoelectric Properties of (Bi_(0.5)Na_(0.5))TiO_3-(Bi_(0.5)K_(0.5))TiO_3 Systems[J].Japanese journal of applied physics,1999(9B):5564-5567.
[3] Zhao M L;Wang C L;Zhong W L et al.Ferroelectric, Piezoelectric and Pyroelectric Properties of Sr1+ xBi4- x- Ti4- xTaxO Ceramics (x=0- 1)[J].Japanese Journal of Applied Physics,2002,41:1455-1458.
[4] Aree Herabut;Ahmad Safari .Processing and electromechanical properties of (Bi_0.5Na_0.5)_(1-1.5x)La_xTiO_3 ceramics[J].Journal of the American Ceramic Society,1997(11):2954-2958.
[5] T.Takenaka .Piezoelectric Properties of Some Lead-Free Ferroelectric Ceramics[J].Ferroelectrics: Letters Section,1999(1/4):87-98.
[6] 初宝进,李国荣,殷庆瑞,张望重,陈大任.非化学计量和掺杂对(Na1/2 Bi1/2)0.92Ba0.08 TiO3 陶瓷电性能的影响[J].物理学报,2001(10):2012-2016.
[7] 赵明磊,王春雷,钟维烈,王矜奉,陈洪存.溶胶-凝胶法制备Bi0.5Na0.5TiO3陶瓷及其电学特性[J].物理学报,2003(01):229-232.
[8] 赵明磊,王春雷,王矜奉,陈洪存,钟维烈.溶胶-凝胶法制备的高压电常数(Bi0.5 Na0.5)1-x BaxTiO3系无铅压电陶瓷[J].物理学报,2004(07):2357-2362.
[9] Kuharuangrong S. .Effect of La and K on the microstructure and dielectric properties of Bi0.5Na0.5TiO3-PbTiO3[J].Journal of Materials Science,2001(7):1727-1733.
[10] Suchanicz J.;Kudzin AY.;Kus C.;Gavshin MG. .Delectric properties of (Na0.5Bi0.5)(1-x)MexTiO3 ceramics near morphotropic phase boundary[J].Journal of Materials Science,2001(8):1981-1985.
[11] 赵明磊,钟维烈,王春雷,王矜奉,张沛霖.钛酸铋钠系铁电体的相变研究[J].物理学报,2002(08):1856-1860.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%