对 Ni/MH电池在 1C充放电和 1C充电 10C放电条件下的循环寿命进行了考察,结果表明 10C放电条件下电池循环寿命只有 76次.对 10C放电循环前后电池内阻、正负极电位、负极性能 变化和贮氢合金腐蚀行为进行了研究.结果表明由于 10C放电条件下电池的温度较高,导致合金 腐蚀速度增加.而合金的腐蚀消耗电解液,使电池内阻增加,负极性能恶化,电池寿命发生衰减.
参考文献
[1] | Soria M L;Chacon J .Metal hydride electrodes and Ni/MH batteries for automotives high power applications[J].Journal of Power Sources,2001,102:97-104. |
[2] | Luisa Soria M;Joaquin Chacon et al.Nickel metal hydrides batteries for high power applications[J].Journal of Power Sources,2001,96:68-75. |
[3] | Z.Q.Zhou;G.W.Lin .Degradation behavior of foamed nickel positive electrodes of Ni-MH batteries[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,1999(0):795-798. |
[4] | Laure Le Guenne;Patrick Bernard .Life duration of Ni- MHcells for high power applications[J].Journal of Power Sources,2002,105:134-138. |
[5] | P. Leblanc;C. Jordy;B. Knosp;P. Blanchard .Mechanism of alloy corrosion and consequences on sealed nickel-metal hydride battery performance[J].Journal of the Electrochemical Society,1998(3):860-863. |
[6] | Patrick Bernarde .Effects on the positive electrode of the corrosion of AB5 alloys in nickel- metal- hydride batteries[J].Journal of the Electrochemical Society,1998,145:456-458. |
[7] | 陈永辉,魏进平,高峰,周伟,张允什,周作祥.MH-Ni电池高倍率循环寿命影响因素探讨[J].电源技术,2001(z1):142-145. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%