采用溶液浸渍法在ITO导电玻璃表面的多孔TiO2薄膜上沉积了FeS2薄膜.使用Fe2O3粉末保护裸露在外的ITO导电膜在硫气氛中热处理后,制得了FeS2/TiO2复合薄膜.应用B531/H数显测厚指示表、数字式四探针测试仪、XJCM-8太阳电池测试仪等研究了FeS2/TiO2复合薄膜的厚度、ITO导电玻璃的电阻率以及FeS2/TiO2复合薄膜的光电性能.结果表明:此方法制得的FeS2/TiO2复合薄膜具有良好的光电性能;且ITO导电膜的电阻率变化较小.因而适宜制备色素增感太阳能电池(DSSC).
参考文献
[1] | ORegan B;Gr(a)tzel M .A low-cost,high-efficiency solar cell based on dye-sensitized colloidal TiO2 films[J].Nature,1991,353:737-739. |
[2] | Nakamura S.;Yamamoto A. .Electrodeposition of pyrite(FeS2) thin films for photovoltaic cells[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2001(1/4):79-85. |
[3] | Seehra S S;Montano P A;Seehra M S.Preparation and characterization of thin films of FeS2[J].JOURNAL OF MATERIALS SCIENCE,1979(04):2761-2673. |
[4] | 黄伟,孟亮.FeS2薄膜光电性能研究进展[J].太阳能学报,2001(04):494-499. |
[5] | Hopfner C.;Ennaoui A.;Pettenkofer C.;Fiechter S.;Tributsch H.;Ellmer K. .STOICHIOMETRY, PHASE AND ORIENTATION-CONTROLLED GROWTH OF POLYCRYSTALLINE PYRITE (FES2) THIN FILMS BY MOCVD[J].Journal of Crystal Growth,1995(3/4):325-334. |
[6] | 陈文梅,赵修建.溶胶凝胶法制备TiO2多孔纳米薄膜[J].武汉工业大学学报,2000(01):6-9. |
[7] | 王瑞斌,戴松元,王孔嘉.纳米TiO2性能表征及在染料敏化纳米薄膜太阳电池中的应用[J].高技术通讯,2003(01):50-52. |
[8] | Smestad G;Ennaoui A et al.Photoactive Thin Film Semiconducting Iron Pyrite Prepared by Sulfurization of Iron Oxides[J].Solar Energy Materials,1990,20(03):149-165. |
[9] | 黄伟,刘艳辉,孟亮.厚度对FeS2薄膜的光电性能的影响[J].太阳能学报,2002(05):533-537. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%