本文通过化学液相还原法采用不同的阴离子还原剂制备了超级电容器电极材料二氧化锰.实验表明,还原剂酸碱度的不同对产物表观颜色也有着明显影响.TEM表明所制备的MnO2均为棒状体,以NaHSO3还原所制备的样1分布最均匀,通过电化学测试比较,样1表现出更好的电容特性,在电位窗口0～1.0V、电流密度为5 mA·cm-2时,其首次放电比容值为255.59 F·g-1,在循环700次后比容值为242.57 F·g-1,容量损失仅5.12%.
参考文献
| [1] | Wu NL. .Nanocrystalline oxide supercapacitors[J].Materials Chemistry and Physics,2002(1/3):6-11. |
| [2] | HU C C;TSOU T W .Capacitive and textural characteristics of hydrous manganese oxide prepared by anodic deposition[J].Electrochimica Acta,2002,47:3523-3532. |
| [3] | Prasad KR;Miura N .Electrochemically synthesized MnO2-based mixed oxides for high performance redox supercapacitors[J].Electrochemistry communications,2004(10):1004-1008. |
| [4] | Khomenko V;Raymundo P E;Beguin F .Optimisation of an asymmetric manganese oxide/activated carbon capacitor working at 2V in aqueous medium[J].Journal of Power Sources,2006,153(01):183-190. |
| [5] | Yi-Shiun Chen;Chi-Chang Hu;Yung-Tai Wu .Capacitive and textural characteristics of manganese oxide prepared by anodic deposition: effects of manganese precursors and oxide thickness[J].Journal of solid state electrochemistry,2004(7):467-473. |
| [6] | Lee H Y;Goodenough J B .Supercapacitor Behavior with KCl Electrolyte[J].Journal of Solid State Electrochem,1999,144(01):220-223. |
| [7] | Toupin M.;Brousse T.;Belanger D. .Influence of microstucture on the charge storage properties of chemically synthesized manganese dioxide[J].Chemistry of Materials,2002(9):3946-3952. |
| [8] | 闪星,董国君,景晓燕,张密林.新型超大容量电容器电极材料一纳米水合MnO2的研究[J].无机化学学报,2001(05):669-674. |
| [9] | Ye C;Lin ZM;Hui SZ .Electrochemical and capacitance properties of rod-shaped MnO2 for supercapacitor[J].Journal of the Electrochemical Society,2005(6):A1272-A1278. |
| [10] | Shu-Juan Bao;Ben-Lin He;Yan-Yu Liang;Wen-Jia Zhou;Hu-Lin Li .Synthesis and electrochemical characterization of amorphous MnO_2 for electrochemical capacitor[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):305-309. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%