研究了(Fe0.5Co0.5)73.5Nb2V1Si13.5B9Cu1合金经不同温度退火后的结构及磁谱曲线.XRD分析表明,随着退火温度的升高,晶化相体积增加;同时晶格常数减少说明更多的Co溶入到晶化相α-FeCo(Si)中.用阻抗分析仪测量了合金在1kHz-10MHz范围的磁谱曲线.结果表明,合金的截止使用频率可达103～106Hz,且随退火温度的升高,合金的截止使用频率逐渐提高,但初始磁导率μi和截止使用频率f0的乘积保持为常数,用畴壁运动方程及畴壁钉扎理论对此进行了解释.并讨论了进一步提高合金高频性能的途径.
参考文献
| [1] | Yoshizawa Y;Oguma S;Yamauchi Y .New Fe-based Soft Magnetic Alloys Composed of Ultrafine Grain Structure[J].Journal of Applied Physics,1988,64:6044-6047. |
| [2] | Herzer G. .Grain structure and magnetism of nanocrystalline ferromagnets[J].IEEE Transactions on Magnetics,1989(5):3327-3329. |
| [3] | Mao X Y;GAO W L;Y W Du et al.Effect of Co substitution for Fe on the magnetization process of nanocrystalline Fe-Nb-B alloys[J].Journal of Magnetism and Magnetic Materials,2004,271:286-289. |
| [4] | W. Qin;Y. F. Zhang;Y. W. Du .Permeability-frequency spectra of Nanoperm alloys under different heat treatment conditions[J].Journal of Magnetism and Magnetic Materials,2004(1/2):174-181. |
| [5] | Liang X B;Jaroslaw F et al.Effect of the substitution of Fe by Co on the magnetic properties and microctruture of nanocrystalline (Fe1-xCox)86Hf7B6Cu1[J].Journal of Magnetism and Magnetic Materials,2004,284:86-91. |
| [6] | 廖绍彬.铁磁学[M].北京:科学出版社,1988 |
| [7] | 王光建 .天津大学硕士学位论文[D].天津:天津大学,2006. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%