采用溶胶凝胶法合成了Sr3A12O6:Eu2+,Dy3+长余辉发光材料,利用Ⅹ射线衍射仪(XRD)对材料的物相进行了分析,采用荧光分光光度计、照度计测定了样品的发光特性.XRD结果表明:随着煅烧温度的升高,SrCO3杂相的衍射峰越来越弱,Sr3Al2O6相的衍射峰越来越强,1200℃时发光基质为纯的Sr3Al2O6相,1250℃时出现新的SrAl2O4杂相.激发光谱和发射光谱结果表明:长余辉发光材料的激发峰位于473 nm,发射峰位于612 nm,归属于Eu2+的4f65d1→4f7特征发光.温度升至1250℃时,Eu2+的发射峰为612 nm和520 nm,后者归属于Eu2+在发光基质SrAl2O4中的发光.综合分析得制备Sr3Al2O6:Eu2+,Dy3+发光材料合适的煅烧温度为1200℃,在此温度下,材料具有较好的初始亮度和余辉时间.
The Sr3Al2O6:Eu2+,Dy3+ red-emitting phosphors were prepared by sol-gel method.The crystal structure were characterized by X-ray diffraction(XRD).The excitation,emission and afterglow spectra were investigated by fluorescence spectrophotometer techniques.The results of XRD analysis show that Sr3Al2O6 phase increases with the increase of calcined temperature,and the amount of SrCO3 crystalline phase decreases.The excitation peak of Sr2.95Al2O6:0.02Eu2+,0.03Dy3+ phosphor is at 473 nm,and samples have the similar emission spectra with peak at 612 nm attributed 4f65d1→4f7 of divalent europium under 1200℃.There is a new emission peak at 520 nm at 1250℃,due to the divalent europium activated by SrAl2O4phosphor.The sample with optimized properties is prepared at 1200℃ on the basis of comprehensive analysis.
参考文献
| [1] | Abbruscato V .Optical and electrical properties of SrAl2O4:Eu2+[J].Electrochemistry Society,1971,118(06):930-934. |
| [2] | Matsuzawa T.;Takeuchi N.;Murayama Y.;Aoki Y. .NEW LONG PHOSPHORESCENT PHOSPHOR WITH HIGH BRIGHTNESS, SRAL2O4-EU2+,DY3+[J].Journal of the Electrochemical Society,1996(8):2670-2673. |
| [3] | Lin J;Baerner K .Tunable photoluminescence in sol-gel derived silica xerogels[J].Materials Letters,2000,46(2-3):86-92. |
| [4] | LIN Jun;YU Min;LIN Cui-kun et al.Multiform oxide optical materials via the versatile pechini-type sol-gel process:synthesis and characteristics[J].Physical Chemistry C,2007,111(16):5835-5845. |
| [5] | 孙家跃;杜海燕;胡文祥.固体发光材料[M].北京:化学工业出版社,2003:548-555. |
| [6] | Palilla F C;Luvine A K;Tomkus M R .Fluorescent properties of alkaline earth aluminates of the type MAI2O4 activated by divalent europium[J].Electrochem Society,1968,115(06):642-644. |
| [7] | 吕兴栋,舒万艮,方勤.基质组成对xSrO·yAl2O3∶Eu2+,Dy3+发光性能的影响[J].稀有金属材料与工程,2007(01):63-67. |
| [8] | Katsuzawa T;Sasajima K;Nabae T et al.Characteristics of Strontium Aluminate Crystals Used for Lung-Duration Phosphors[J].Communications of American Ceramic Society,1998,81(02):413-416. |
| [9] | Zhang P;Xu MX;Zheng ZT;Sun B;Zhang YH .Rapid formation of red long afterglow phosphor Sr3Al2O6 : Eu2+, Dy3+ by microwave irradiation[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2007(2/3):159-164. |
| [10] | Pallavi Page;Rahul Ghildiyal;K. V. R. Murthy .Synthesis, characterization and luminescence of Sr_3Al_2O_6 phosphor with trivalent rare earth dopant[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2006(10):1854-1860. |
| [11] | 赵晓玲,黄平,郝虎在,崔彩娥.硫掺杂对Sr3Al2O6红色长余辉发光材料性能的影响[J].中国稀土学报,2008(02):217-220. |
| [12] | 苏锵.稀土化学[M].郑州:河南科学技术出版社,1993:P13-P14. |
| [13] | 吕兴栋 .铝酸锶长余辉发光材料的超细粉体制备、构效关系及其应用研究[D].中南大学,2005. |
| [14] | Schulze A R;Mueller-Buschbaum H .Zur Struktur von monoklinem SrAl2O4[J].Zeitschrift fuer Anorganische und Allgemeine Chemie,1981,475:205-210. |
| [15] | Chakoumakos B C;Lager G A;Fernandez-Baca J A .Refinement of the structures of Sr3Al2O6 and the hydrogarnet Sr3Al2(O4D4)3 by Rietveld analysis of neutron powder diffraction data[J].Acta Crystallographica Section C,1992,48:414-419. |
| [16] | Hong G Y;Jeon B S;YooY K et al.Photoluminescence characteristics of spherical Y203:Eu phosphors by aerosol pyrolysis[J].Electrochemistry Society,2001,148(11):H161-H166. |
| [17] | Aitasalo T.;Deren P.;Holsa J.;Jungner H.;Krupa JC.;Lastusaari M. Legendziewicz J.;Niittykoski J.;Strek W. .Persistent luminescence phenomena in materials doped with rare earth ions[J].International Journal of Quantum Chemistry,2003(1/2):114-122. |
| [18] | Yamamoto H;Matsuzawa T .Mechanism of long phosphorescence of SrAl2O4:Eu2+, Dy3+ and CaAl2O4:Eu2+, Nd3+[J].Journal of Luminescence: An Interdisciplinary Journal of Research on Excited State Processes in Condensed Matter,1997(0):287-289. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%