研究了Si含量对Fe87-x Cu1 Nb3 Six B9合金经不同方式退火后磁性能的影响.结果表明:随Si含量的增加,Fe87-x Cu1 Nb3 Six B9合金经普通退火后软磁性能逐渐得到优化;经磁退火后可感生出单轴磁各向异性,且磁退火特征随Si含量的增加而逐渐明显.根据横磁退火实验结果计算出的感生磁各向异性值K,,则由26.7J/m3(Si=9.5at%)降低至14.1J/m3(Si=13.5at%).由实验数据的分析认为Fe87-x Cu1 Nb3 Six B9合金在高Si含量时经普通退火或纵磁退火后呈现优异的软磁特性,归因于析出的α-Fe(Si)相晶粒具有小的磁晶各向异性K,从而导致合金具有更低的有效磁各向异性常数
The effect of the Si content on magnetic properties for nanocrystalline Fe87-x Cu1 Nb3 Six B9 alloys annealed in different methods has been investigated.It was found that the magnetic properties of Fe87-x Cu1 Nb3 Six B9 alloys annealed in normal methods were obviously improved with the increasing Si content.Annealing under a magnetic field can induce an uniaxial anisotropy and the magnetic annealing feature was increased with the increasing of Si content.According to the results calculated from traversal magnetic annealing,the magnitude of induced magnetic anisotropy Ku was induced from 26.7J/m3(Si = 9.5at%)to 14.1J/m3(Si = 13.5at%).Analysis of the experimental data suggests that the excellent soft properties for Fe87-x Cu1 Nb3 Six B9 alloys with more Si content after normal or magnetic annealing are atmuch lower effective magnetic anisotropy < K >.
参考文献
| [1] | Yoshizawa Y;Oguma S;Yamauchi K .New Fe-based soft magnetic alloys composed of ulrafine grain structure[J].Applied Physics,1988,64(10):6044. |
| [2] | Herzer G .Nanocrystalline Soft Magnetic Materials[J].Magnetism and Magnetic Materials,1996,A157/158:133-136. |
| [3] | Krivosik P.;Appino C.;Sasso CP.;Pasquale M. .Modeling of interactions in amorphous and nanocrystalline alloys with induced anisotropy[J].Journal of Magnetism and Magnetic Materials,2002(2):1093-1096. |
| [4] | Yoshizawa Y.;Yamauchi K. .Effects of magnetic field annealing on magnetic properties in ultrafine crystalline Fe-Cu-Nb-Si-B alloys[J].IEEE Transactions on Magnetics,1989(5):3324-3326. |
| [5] | Herzer G .Magnetic field induced anisotropy in nanocrystalline Fe-Cu-Nb-Si-B alloys[J].Materials Science and Engineering,1994,A181/A182:876-879. |
| [6] | Hono K;Li J L;Ueki Y et al.Atom probe study of the crystallization process of an Fe73.5Si13 5B9Nb3Cul amorphous alloy[J].Applied Surface Science,1993,67(04):398-406. |
| [7] | Herzer G. .Grain structure and magnetism of nanocrystalline ferromagnets[J].IEEE Transactions on Magnetics,1989(5):3327-3329. |
| [8] | Hernando A.;Vazquez M.;Barandiaran JM.;Herzer G.;Marin P. .Thermal dependence of coercivity in soft magnetic nanocrystals[J].Physical Review.B.Condensed Matter,1998(1):366-370. |
| [9] | Zhi Q Z;Dong B S;Chen W Z et al.Elevated temperature initial permeability study of Fe73.5 Cu1 Nb3 Si13.5 B9 alloy[J].Materials Science and Engineering,2007,A448:249-242. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%