用纯Fe片做阳极,研究在纯Cu基体上采用高频(20-140kHz)脉冲电流获得的Fe-Co合金薄膜组织和性能与沉积参数的关系,分析了阳极在沉积过程中对镀层组织和性能的作用机理.电子探针(EPMA)照片表明,提高占空比,镀层粗糙度增加.扫描电镜(SEM)结果进一步表明,提高脉冲频率可以显著增加沉积速率,使镀层变厚,因此可采用高频脉冲来探索高速电镀技术.采用X射线衍射仪(XRD)分析了镀层结构,发现提高脉冲频率,fcc(111)与bcc(110)相对强度先减小后增大.振动样品磁强计(VSM)测试结果表明,140 kHz沉积的镀层矫顽力均低于20和80 kHz,即高频可以降低镀层矫顽力.虽然沉积的Fe65Co35合金薄膜饱和磁化强度高达2.12 T,但矫顽力较高.比较其它阳极沉积的FeCo合金薄膜,发现选用可溶性Co阳极比较适合.
参考文献
| [1] | Tetsuya Osaka;Toru Asahi;Jun Kawaji;Tokihiko Yokoshima .Development of high-performance magnetic thin film for high-density magnetic recording[J].Electrochimica Acta,2005(23):4576-4585. |
| [2] | Osaka Tetsuya .Recent development of magnetic recording head core materials by plating method[J].Electrochimica Acta,1999(21):3885-3890. |
| [3] | Tetsuya Osaka;Junichi Sayama .A challenge of new materials for next generation's magnetic recording[J].Electrochimica Acta,2007(8):2884-2890. |
| [4] | N. V. Myung;D.-Y. Park;D. E. Urgiles;T. George .Electroformed iron and FeCo alloy[J].Electrochimica Acta,2004(25):4397-4404. |
| [5] | Vilain S;Ebothe J .Growth and topology of Co-Fe and Co-Ni alloy electrodeposits studied by atomic force microscopy[J].Materials Science and Engineering C,2001,15:199-201. |
| [6] | Tetsuya Osaka;Tokihiko Yokoshima;Daizo Shiga .A High Moment CoFe Soft Magnetic Thin Film Prepared by Electrodeposition[J].Electrochemical and solid-state letters,2003(4):C53-C55. |
| [7] | 王子涵,杨滨,马岩,蒋春丽,张鹏程,罗丽珠.脉冲频率对电沉积CoFe合金镀层组织和磁性能的影响[J].兰州理工大学学报,2010(02):10-14. |
| [8] | 陈亚.现代实用电镀技术[M].北京:国防工业出版社,2004:270-271. |
| [9] | 安茂忠.电镀理论与技术[M].哈尔滨:哈尔滨工业大学出版社,2004:178-241. |
| [10] | N.G. Chechenin;E.H. du Marchie van Voorthuysen;J.Th.M. De Hosson .Variation of structure and magnetic properties with thickness of thin Co_(59)Fe_(26)NI_(15) films[J].Journal of Magnetism and Magnetic Materials,2005(2):1539-1542. |
| [11] | Yahui Zhang;Douglas G. Ivey .Characterization of Co-Fe and Co-Fe-Ni soft magnetic films electrodeposited from citrate-stabilized sulfate baths[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2007(1/2):15-22. |
| [12] | Armyano S .Crystallographic structure and magnetic properties of electrodeposited cobalt and cobalt alloys[J].Electrochimica Acta,2000,45:3323-3335. |
| [13] | 田莳.材料物理性能[M].北京:北京航空航天大学出版社,2007:313. |
| [14] | Sulitanu N.;Brinza F. .Excellent soft magnetic two-phase nanocrystalline films for various magnetic devices[J].Sensors and Actuators, A. Physical,2003(1/3):212-216. |
| [15] | 付煜 .超高密度磁记录磁头材料Fe-Co薄膜的研究[D].兰州大学,2006. |
| [16] | Brankovics S R;Bae S E;LITVINOV D .The effect of Fe3+ on magnetic moment of electrodeposited CoFe alloys--Experimental study and analytical model[J].Electrochimica Acta,2008,53:5934-5940. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%