采用化学共沉淀法制备NiZnCu铁氧体时,如果采用NaOH或者氨水作为沉淀剂,会造成Zn2+离子的大量损失.为此,本文选用Na2CO3为沉淀剂制备了名义配方为Ni0.4-xZn0.6CuxFe2O4(x=0,0.05,0.10,0.15,0.20)的铁氧体粉末,并对其结构和磁性能作了研究.实验发现,前驱体粉末在900℃温度下煅烧2小时后皆形成单相铁氧体粉末；样品的饱和磁化强度Ms和矫顽力Hc随着Cu含量的增加而减小,起始磁化率Xi呈现先增加后减小的趋势,在x=0.10时达到最大值.研究表明,Cu的最佳取代量在x=0.10左右.
参考文献
| [1] | 韩志全.叠层片式电感及低温烧结铁氧体的研发进展[J].磁性材料及器件,2004(06):6-10. |
| [2] | 冯唐福,许启明,陈涛.Bi2O3-Nb2O5复合掺杂对NiCuZn铁氧体性能的影响[J].电子元件与材料,2008(03):58-60. |
| [3] | 陈涛,许启明,冯唐福.V2O5含量对MoO3-V2O5复合添加NiCuZn铁氧体性能的影响[J].磁性材料及器件,2008(01):28-31. |
| [4] | Xia A L;Zhang H L .Effects of excessive Zn2 + ions on intrinsic magnetic and structural properties of Nio,2 Zn0.6 Cu0,2 Fe2 O4 powder prepared by chemical co-precipitation method[J].Current Applied Physics,2010,10:825. |
| [5] | Chu N J;Wang X Q;Liu Y P.Magnetic properties of low Mn-doped NiCuZn nanocrystalline ferrites[J].Journal of Alloys and Compounds,2009:470-438. |
| [6] | Roy P K;Bera J.Electromagnetic properties of samarium-substituted NiCuZn fenrite prepared by auto-combustion method[J].Journal of Magnetism and Magnetic Materials,2009:321-247. |
| [7] | 周志刚.铁氧体磁性材料[M].北京:科学出版社,1981:34. |
| [8] | 张有纲;黄永杰;罗迪民.磁性材料[M].成都:成都电 讯工程学院出版社,1988:21. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%