综述了有关核聚变反应堆材料的辐照损伤问题的研究, 主要包括国产316L奥氏体不锈钢中氦的扩散与氦泡形核生长的研究、 316L及低活化FeCrMn合金的高能Ar离子辐照缺陷与空洞肿胀的研究、近期开展的低活化马氏体钢和氧化物颗粒弥散强化合金的高能Ne离子辐照损伤和效应的研究成果.
参考文献
[1] | Ulllmaier H.Radiation Effects,1983,78:1. |
[2] | Zhang C H,Chen K Q,Wang Y S,et al.J Nucl Mater,1997,245:210. |
[3] | Zhang C H,Chen K Q,Wang Y S,et al.J Nucl Mater,1998,263:1 623. |
[4] | Zhang C H,Chen K Q,Wang Y S,et al.Nucl Instr and Meth,1998,B135:256. |
[5] | Chen K Q,Zhang C H,Quan J M,et al.J Nucl Mater,1996,240:70. |
[6] | Chen K Q,Wang Y S,Quan J M,et al.J Nucl Mater,1994,212:345. |
[7] | Zhang C H,Chen K Q,Zhu Z Y.Nucl Instr and Meth,2000,B169:64. |
[8] | 张崇宏,陈克勤,王引书等.物理学报,1997,46(9):1 774. |
[9] | 张崇宏,陈克勤,王引书等.原子核物理评论,2001,18(1):50. |
[10] | Zhang C H,Chen K Q,Wang Y S,et al.In:Proc.7th China-Japan Symposium on Materials for Advanced Energy Systems & Fission and Fusion Engineering.Eds.Wang Z G,Zhu Z Y,Jin G M.World Scientific Publishing Co.,2003,53-63. |
[11] | Zhang C H,Wang Y S,Chen K Q,et al.Mater Sci Forum,2004,475-479:1 459. |
[12] | Zhang C H,Chen K Q,Wang Y S,et al.J Nucl Mater,2000,283-287:259. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%