在草酸和硫酸电解液中分别制备了孔径为40 nm和20 nm左右的多孔氧化铝模板,用直流电化学沉积的方法,在模板孔洞内电解沉积Zn,对其进行高温下的氧化,可得到高度有序的ZnO纳米线.扫描电子显微镜观察显示,多晶的Zn纳米线均匀地填充到多孔氧化铝六角排布的孔洞里,直径与模板孔径相当.X射线衍射谱测量证实,制备的Zn纳米线和ZnO纳米线均为多晶结构,并且对比了模板孔径对纳米线结构的影响.测量了多孔氧化铝厚膜和Zn/Al2O3组装体的吸收光谱,发现其在红外波段的吸收系数有逐渐降低的趋势.
参考文献
| [1] | McGlynn E,Fryar J,et al.Effect of polycrystallinity on the optical properties of highly oriented ZnO grown by pulsed laser deposition[J].Thin.Solid.Films.,2004,458:330-335. |
| [2] | Sans J A,Segura A,et al.Optical properties of ZnO prepared by pulsed laser deposition[J].Thin.Solid.Films.,2004,453-454:251-255. |
| [3] | Wu X L,Siu G G,et al.Photoluminescence and cathodoluminescence studies of stoichiometric and oxygendeficient ZnO films[J].Appl.Phys.Lett.,2001,78:2285-2287. |
| [4] | Zhang B P,Wakatsuki K,et al.Effect of growth temperature on the characteristics of ZnO epitaxial films deposited by metalorganic chemical vapor deposition[J].Thin.Solid.Films.,2004,449:12-19. |
| [5] | Ryu M K,Lee S H,et al.Postgrowth annealing effect on structure and optical properties of ZnO films grown on GsAs substrates by the radio frequency magnetron sputtering[J].J.Appl.Phys.,2002,92:154-158. |
| [6] | Vigue F,Venegues P,et al.Defect characterization in ZnO layers grown by plasma-enhanced molecular-beam epitaxy on (0001) sapphire substrates[J].Appl.Phys.Lett.,2001,79:194-196. |
| [7] | Deng Kaifa,Shi Dufang,Jiang Meiping,et al.Progress in the study of photonic crystal[J].Chinese Journal of Quantum Electronics,(量子电子学报),2004,21(5):555-564 (in Chinese). |
| [8] | Lee C J,Lee T J,et al.Field emission from well-aligned zinc oxide nanowires grown at low temperature[J].Appl.Phys.Lett.,2002,81:3648-3650. |
| [9] | Lyu Seung Chul,Ye Zhang,et al.Low temperature growth and photoluminescence of well-aligned zinc oxide nanowires[J].Chem.Phys.Lett.,2002,363:134-138. |
| [10] | Wu Jinjen,Lin Saichang,et al.Catalyst-Free growth and characterization of ZnO nanorods[J].J.Phys.Chem.B,2002,106:9545-9551. |
| [11] | Li Y,Meng G W,et al.Ordered semiconductor ZnO nanowire arrays and their photoluminescence properties[J].Appl.Phys.Lett.,2000,76:2011-2013. |
| [12] | Li Y,Cheng G S,et al.Fabrication of highly ordered ZnO nanowire arrays in anodic alumina membranes[J].J.Mater.Res.,2000,15:2305-2308. |
| [13] | Shi G,et al.Photoluminescence of ZnO nanoparticles in alumina membrane with orderedpore arrays[J].Soli.Stst.Comm.,2000,115:253-256. |
| [14] | Zheng M J,Zhang L D,et al.Fabrication and optical properties of large-scale uniform zinc oxide nanowire arrays by one-step electrochemical deposition technique[J].Chem.Phys.Lett.,2002,363:123-128. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%