以煤焦油沥青与吡啶硼烷为原料,在400 ℃,1 MPa压力下,反应10 h制备出了硼取代聚芳烃中间相.考察了硼含量对中间相性质及微观结构的影响.发现在同一热缩聚条件下随着硼添加量的增加,中间相沥青的收率下降,但中间相小球的收率却相应提高,球径逐渐减小.实验结果表明,硼促进了中间相的形成,并且起着交联剂的作用.
参考文献
[1] | Hoffmann W R;Hiittinger K J .Modeling of the apparent viscosity of pitches and mesophases at linear temperature increase up to 500 ℃[J].Carbon,1993,31:263-268. |
[2] | Fujiura R.;Komatsu M.;Mochida I.;Kojima T. .MECHANICAL PROPERTIES OF BINDERLESS CARBON MOULD PREPARED FROM HEAT-TREATED MESOPHASE PITCH OF CONTROLLED GRAIN SIZE[J].Carbon: An International Journal Sponsored by the American Carbon Society,1995(8):1061-1068. |
[3] | M. BRAUN;K. J. HUETTINGER .SINTERING OF POWDERS OF POLYAROMATIC MESOPHASE TO HIGH-STRENGTH ISOTROPIC CARBONS: Ⅲ. POWDERS BASED ON AN IRON-CATALYZED MESOPHASE SYNTHESIS[J].Carbon: An International Journal Sponsored by the American Carbon Society,1996(12):1473-1491. |
[4] | Ehrburger P;Baranne P;Lahaye J .Inhibition of the oxidation of carbon- carbon composite by boron oxide[J].Carbon,1986,24:495-499. |
[5] | 郭全贵 .炭/陶复合材料高温自愈合抗氧化行为及其结构设计研究[D].中国科学院山西煤炭化学研究所,1998. |
[6] | Fecko D L;Jones L E;Thrower P A .The formation and oxidation of BC3,a new graphitelike material[J].Carbon,1993,31:637-644. |
[7] | Eichner T;Barun M;Huttinger K J .Element-substituted polyaromatic mesophase:I boron-substitution with the pyridine-borane comples[J].CARBON,1996,34:1367-1381. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%