以酚醛树脂(Phenol-formaldehyde resin, PF)和B4C为原料制备的高温粘接剂,对石墨材料进行粘接,并在200 ℃、800 ℃和1 500 ℃进行热处理.对粘接样品的强度测试结果表明,粘接部件具有较高的耐热温度和粘接强度.利用扫描电镜(SEM)和X射线衍射(XRD)对不同温度热处理后的粘接界面结构形貌及粘接剂组成进行了分析,研究了酚醛树脂中的B4C添加剂在粘接过程中的结构变化及其对提高粘接性能的作用机理.
参考文献
| [1] | Kakegawa H;Otani S;Maeda Y.Adhesion structure of graphite using COPNA resins[A].,1987:231-232. |
| [2] | Kravetskii G A;Anikin L T;Demin A V.High-temperature bonding of parts made of carbon and carbon-ceramic materials[A].,1995:798-799. |
| [3] | Gladkikh S N;Curov A A;Fekhvetdinov F A K.Highly heat-resistant cold-curing adhesives[J].Plasticheskie Massy,1991(10):24-25. |
| [4] | Anikin L T;Kraretskii G T;Kuzina O A et al.Heat-resistant adhesive for joining of carbon materials[J].Plaste Kautsh,1992,39(02):54-56. |
| [5] | G S 布拉德;H R 克劳瑟.材料手册[M].北京:科学出版社,1989:902. |
| [6] | 王荣顺.酚醛树脂热裂解产物的结构研究[J].高等学校化学学报,1990(10):1161. |
| [7] | KIMBERLY A. TRICK;TONY E. SALIBA .MECHANISMS OF THE PYROLYSIS OF PHENOLIC RESIN IN A CARBON/PHENOLIC COMPOSITE[J].Carbon: An International Journal Sponsored by the American Carbon Society,1995(11):1509-1515. |
| [8] | 谢有赞.碳石墨材料工艺[M].长沙:湖南大学出版社,1988:379. |
| [9] | 王孟钟;黄应昌.胶粘剂应用手册[M].北京:化学工业出版社,1987:8. |
| [10] | 薛改凤,陶着,王丽芳,陈文.用混合磨碎法制备高强、耐氧化的碳-陶复合材料的研究[J].新型碳材料,1989(03):1-8. |
| [11] | Woodley R E .The reaction of boronated graphite with water vapor[J].Carbon,1969,7(05):609-613. |
| [12] | Sheehan J E .Oxidation protection for carbon fiber composites[J].Carbon,1989,27(05):709-715. |
| [13] | Mckee D W;Spiro C L;Lamby E J .The effects of boron additives on the oxidation behavior of carbons[J].Carbon,1984,22(06):507-511. |
| [14] | 天津化工研究院.无机盐工业手册[M].北京:化学工业出版社,1979:239. |
| [15] | Lowee C E .Solid solution of boron in graphite[J].Journal of the American Ceramic Society,1967,50(03):142. |
| [16] | 李崇俊,马伯信.碳化硼对碳/碳复合材料的催化石墨化作用[C].第三届全国新型炭材料学术研讨会论文集,1997:365～369. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%