制备了一系列掺杂石墨并研究了其导热性能。实验结果表明，与相同条件下制得的纯石墨相比，掺杂石墨的导热系数均有较大的提高。掺杂钛组元可使石墨材料的导热性能有所提高，而硅组元的加入可大大提高石墨材料的导热性能，硼组元的加入则使石墨材料的导热性能明显下降，这与硼原子可溶入石墨晶格而造成晶格缺陷有关。XRD分析结果表明掺杂石墨都具有大的晶格尺寸，高的石墨化程度，这与掺杂组元的催化石墨化作用有关。
Thermal conductivity of some doped graphite was investigated inorder to discuss the effect of dopants on the doped graphite. Results show that the doped graphite exhibits higher thermal conductivity than the pure graphite produced by same process. Thermal conductivity of the graphite can be improved by doping titanium. And doping titanium and silicon simultaneously into the graphite can improve the thermal conductivity much greatly. Adding boron can result in the decrease of thermal conductivity for boron can go into the lattice and form defects of graphite lattice. XRD analysis shows that the doped graphite has large crystalline and high graphitization degree.
参考文献
| [1] | Burtseva A;Chugunov O K.Resistance of carbon-based materials for the ITER divertor under different radiation fluxes[J].Journal of Nuclear Materials,1992(191-194):309-314. |
| [2] | Hugh O.Pieson Hand Book of Carbon,Graphite,Diamond and Fullerenes-Properties,Processing and Applications[M].USA:Noyes Publication,1990 |
| [3] | Quangui Guo;Lang Liu;Jingren song.Preparation and properties of the composites characterized by functionally gradient SiC coatings and graphite substrats[A].,1999 |
| [4] | Garcia-Rosales C;Roth J;Behrisch R.Sputtering and surface composition modifications of Ti doped graphite RG-Ti at temperatures up to 2000?K[J].Journal of Nuclear Materials,1994(212-215):1211-1217. |
| [5] | Qian J P;Deng X W.Recent results on fusion reactor materials research in China[J].Journal of Nuclear Materials,1994(212-215):11-17. |
| [6] | Qian J P;Liu X;Li P Y.Thermal shock of carbon based materials and coatings under high heat flux[J].Journal of Nuclear Materials,1992(191-194):340-345. |
| [7] | Wolf R.Boronized and siliconized graphites-material processing and effects on properties[J].Journal of Nuclear Materials,1994(212-215):1174-1177. |
| [8] | Garcia-Rosales C;Roth J.Chemical sputtering of pyrolytic graphite and boron doped graphite USB15 at energies between 10 and 1000?eV[J].Journal of Nuclear Materials,1994(212-215):450-461. |
| [9] | Enweani BN.;Haasz AA.;Davis JW. .THERMAL DIFFUSIVITY CONDUCTIVITY OF DOPED GRAPHITES[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,1995(3):245-253. |
| [10] | Rubel M;Almqvist N;Wienhold P.Behaviour of Si and Ti doped carbon composites under exposure to the deuterium plasma[J].Journal of Nuclear Materials,1998(258-263):787-792. |
| [11] | Burtseva T B;Chugunov O K.Resistance of carbon-based materials for the ITER divertor under different radiation fluxes[J].Journal of Nuclear Materials,1992(191-194):309-314. |
| [12] | 中国化工百科全书委员会.中国化工百科全书[M].北京:化学工业出版社,1998 |
| [13] | 张光晋,郭全贵,刘占军,刘朗.掺钛石墨导电性及其微观结构的研究[J].新型炭材料,2000(04):35-38. |
| [14] | 萨姆索诺夫.难熔化合物手册[M].北京:中国工业出版社,1965 |
| [15] | 李圣华.碳石墨材料的制品[M].北京:冶金工业出版社,1986 |
| [16] | 陈骏凌 .HT-7U托卡马克第一壁材料的制备与表征[D].中国科学院合肥等离子体研究所,2000. |
| [17] | 郭全贵 .炭/陶复合材料高温自愈合抗氧化行为及其结构设计研究[D].中国科学院山西煤炭化学研究所,1998. |
| [18] | 项启贤 .再结晶石墨的性能[J].碳素译从,1992,13(01):1-5. |
| [19] | 日本炭素材料学会;中国金属学会炭素材料专业委员会.炭素材料入门[M].,1999 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%