为了研究气相生长纳米炭纤维在炭/炭复合材料制备中的应用,采用均热式化学气相沉积技术,以针刺PAN炭纤维薄毡为基体,二茂铁为催化剂前驱体,丙烯为碳源,氮气为载气,在炉压1.0kPa～1.3kPa,沉积温度880℃、920℃下进行了Fe催化PAN炭纤维原位生长纳米炭纤维的实验.经不同时间沉积后的样品在扫描电镜(SEM)下进行观察,发现880℃时沉积4h后在PAN炭纤维周围生成大量的原位生长纳米炭纤维,而在920℃时因催化剂失效导致热解炭对Fe催化剂颗粒包覆,形成颗粒状热解炭.
参考文献
| [1] | 范月英,成会明,苏革,魏永良,沈祖洪.气相生长纳米炭纤维的研究进展[J].新型炭材料,1999(02):14-20. |
| [2] | 李安邦.气相生长炭纤维[J].新型炭材料,1999(03):79. |
| [3] | Downs W B;Bakers R T K.Mixed carbon fiber-carbon filament preforms for a new generation of advanced composites[A].Pennsylvania(USA):Penn State University,University Park,1989:268-269. |
| [4] | Downs W B;Bakers R T K.Preserving carbon fiber strength during CVD of catalytic carbon filament[A].Santa Barbara,University of California,1991:318-319. |
| [5] | Mcallister P;Wolf E E .Ni-catalyzed carbon infiltration of carbon-carbon substrates[J].Carbon,1992,30(02):189-200. |
| [6] | Richard E Z;Dana T G .An iron catalyst for CVD of methane on carbon fibers[J].Carbon,1992,30(02):295-299. |
| [7] | Rostrup-Nielsen J R;Trimm D L .Mechanisms of carbon formation on nickel-containing catalysts[J].Journal of Catalysis,1977,48:155-165. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%