主要探讨酚醛树脂为前驱物的类玻璃炭,在炭化及石墨化至2 400 ℃过程中,利用透射电子显微镜观察其微结构的变化.发现一些明显的微晶碳层平面完好地堆栈在孔洞周围,这些碳层结晶尺寸在20 nm～200 nm之间.同时,这些碳层平面排列十分整齐并延伸至孔洞的表面,这些排列完好的碳层平面主要是因在小分子物气化过程中所产生.这个气化反应会生成像石墨化应力的效果,导致在孔洞内部及边缘形成高结晶碳层平面.
Phenolic resin was heat-treated up to 2 400 ℃ in an argon flow, leading to the formation of porous graphitized products. The microstructural changes in the graphitized phenolic resin were investigated by transmission electron microscopy. Some oval-shaped crystallites from 20 to 200 nm and with very regular order have been found, which extend to the surface of the pores. In general, the larger the pores, the larger are the crystallites inside them, and there are smaller crystallites between the larger crystallites. The formation of the crystallites is due to the gas evolution reaction, evaporation of which creates an effect analogous to stress graphitization, leading to these highly directional crystallites at the edges and inside the pores.
参考文献
| [1] | Hu HL;Ko TH;Ku WS .Changes in the microstructure and characteristics of carbon/carbon composites with mesophase mesocarbon microbeads added during graphitization[J].Journal of Applied Polymer Science,2005(5):2178-2190. |
| [2] | Manocha L M;Mahl O P .Influence of carbon fiber type and weave pattern on the development of 2D carbon-carbon composites[J].Carbon,1988,26:13-22. |
| [3] | Rellick G S;Adams P M .TEM studies of resin-based matrix microsture in carbon/carbon composites[J].CARBON,1994,32:127-144. |
| [4] | Ko T H;Li C H .The influence of pre-carbonization on the properties of PAN-based carbon fibers deveopled by two-stage contiuous carbonization and air oxidation[J].Polymer Composites,1995,16:224-231. |
| [5] | Ko T H;Jaw J J;Chen Y C .The effect of pyrolysis on the properties of stabilized PAN fabric reinforced phenolic resins for 2D carbon/carbon composites[J].Polymer Composites,1995,16:522-528. |
| [6] | 柯泽豪,卢盈壬.PAN基预氧化纤维不织布增强酚醛树脂制作炭/炭复合材料[J].新型炭材料,2000(04):1-4. |
| [7] | 刘春玲,郭全贵,史景利,刘朗.酚醛纤维在热处理过程中微结构的变化[J].新型炭材料,2004(02):124-128. |
| [8] | Ko T H;Kuo W S;Lu Y R .The influence of post-cure on the properties carbon/phenolic resin cured composites and their final carbon/carbon composites[J].Polymer Composites,2000,21:96-103. |
| [9] | Tzeng SS;Lin W.-C. -- .Mechanical behavior of two-dimensional carbon/carbon composites with interfacial carbon layers[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(12):2011-2019. |
| [10] | Tzeng SS.;Chr YG. .Evolution of microstructure and properties of phenolic resin-based carbon/carbon composites during pyrolysis[J].Materials Chemistry and Physics,2002(2/3):162-169. |
| [11] | Lamidieu P;Monthioux M;Oberlin A .Interfacial phenoena in a glassy carbon/pyrex-glass composites[J].CARBON,1991,29:239-249. |
| [12] | Lausevic Z;Marinkovic S .Mechanical properties and chemistry of carbonization of phenol formaldehyde resin[J].Carbon,1986,24:575-580. |
| [13] | Kimberly A T;Saliba T E .Mechanism of the pyrolysis of phenolic resin in a carbon/carbon composites[J].Carbon,1995,33:1509-1514. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%