利用模压半炭化成型工艺在大气环境下制备出了短切炭纤维增强沥青基C/C复合材料(简称SCFRC).研究了短切炭纤维的体积分数对SCFRC材料的体积密度和力学性能的影响规律.借助光学显微镜和扫描电镜对其微观组织和断口形貌进行了观察,分析了短切炭纤维对SCFRC材料的增强机制.结果表明,当短切炭纤维的体积分数由0%增大到11.8%时,SCFRC材料的力学性能随之呈线性增加;短切炭纤维增强SCFRC材料的机制主要有裂纹偏转效应、桥联效应以及脱粘和拔出效应.
参考文献
| [1] | Fukunaga A.;Komami T.;Ueda S.;Nagumo M. .Plasma treatment of pitch-based ultra high modulus carbon fibers[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(7):1087-1091. |
| [2] | Ruiying Luo;Caili Yang .Effect of preform architecture on the mechanical properties of 2D C/C composites prepared using rapid directional diffused CVI processes[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(12):2221-2228. |
| [3] | Chellappa V;Jang B Z.Development of short carbon fiber/carbon matrix composites[A].,1994:491-498. |
| [4] | 立早.炭纤维增强复合材料[J].新型炭材料,1999(04):79. |
| [5] | 李贺军.炭/炭复合材料[J].新型炭材料,2001(02):79-80. |
| [6] | 蔡大勇,李东春.纤维含量对C／C复合材料力学性能的影响[J].炭素技术,2001(01):16-18. |
| [7] | 沈曾民,迟伟东,赵莉,李晏,刘辉.模压法制备C/C复合材料的研究[J].新型炭材料,1999(03):37-42. |
| [8] | 乔生儒.复合材料细观力学性能[M].西安:西北工业大学出版社,1997:58-61. |
| [9] | 穆柏春.陶瓷材料的强韧化[M].北京:冶金工业出版社,2002:157. |
| [10] | 孙乐民,李贺军,张守阳.沥青基碳／碳复合材料的组织特性[J].无机材料学报,2000(06):1111-1116. |
| [11] | 郭领军,李贺军,薛晖,石振海,李克智.短切炭纤维增强沥青基C/C复合材料的组织特征[J].新型炭材料,2004(02):119-123. |
| [12] | 邹林华,黄勇,黄伯云,黄启忠.C/C复合材料的显微结构及其与工艺、性能的关系[J].新型炭材料,2001(04):63-70. |
| [13] | 孙乐民,李贺军,张守阳.沥青基炭/炭复合材料的弯曲断裂特征[J].新型炭材料,2001(03):28-31,41. |
| [14] | 韩红梅,张秀莲,李贺军,岳珠峰,李克智.炭/炭复合材料高温力学行为研究[J].新型炭材料,2003(01):20-24. |
| [15] | Buckley J D;Edie D D.Carbon-Carbon Materials And Composites[M].New Jersey:Noyes Publications,1993:128. |
| [16] | 李晔,黄启忠,王林山.树脂浸渍法对炭/炭复合材料力学性能的影响[J].新型炭材料,2003(02):117-122. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%