利用SEM和TEM考察了3D C/C复合材料在电弧加热器上烧蚀后的材料表层显微组织结构变化.发现炭纤维和基体炭中的石墨微晶经过烧蚀后都得到了明显的发展.在距烧蚀表面几个纳米的深度范围内形成了高度取向的带状石墨织构,同时,在带状织构中间也形成了许多孔洞和缝隙.在距烧蚀表面几个微米的深度形成了卷曲柱状结构,在这些柱状结构周围有许多缺陷.在纤维和基体炭的界面区域,靠近纤维一侧形成了带状织构,且织构间的缝隙变大.
Textural changes of a 3D carbon/carbon composite after ablation in an arc jet heater were examined under SEM and TEM. It was shown that obvious enlargement of graphite crystallites was generally observed for both carbon fibers and matrix. A highly ordered graphitic ribbon - like texture was developed within a few nanometers of the ablated surface of the carbon fibers with gaps between the ribbons. Crystallites in the form of a round hollow column were pre sent in the matrix of the ablated surface. A ribbon like texture in the interface region near the side of the carbon fibers was observed.
参考文献
| [1] | Fitzer E;Manocha L M.Carbon Fiber Reinforcements and Carbon/Carbon Composites[M].Berlin:Springer and New York:Heidelberg,1997:310-337. |
| [2] | Savage G.Carbon-Carbon Composites[M].London:Chapman& Hall and New York:Glasgow,1992:323-360. |
| [3] | Ellis R A;Lee J C;Payne F M et al.Development of a carboncarbon translating nozzle extension for the RL10B liquid rocket engine[R].AIAA 97-2672 |
| [4] | 李贺军.炭/炭复合材料[J].新型炭材料,2001(02):79-80. |
| [5] | 苏君明.高效高冲质比C/C喷管的应用与进展[J].新型碳材料,1996(04):18-23. |
| [6] | 邹林华,黄勇,黄伯云,黄启忠.C/C复合材料的显微结构及其与工艺、性能的关系[J].新型炭材料,2001(04):63-70. |
| [7] | 黄海明,杜善义,吴林志,王建新.C/C复合材料烧蚀性能分析[J].复合材料学报,2001(03):76-80. |
| [8] | Kratach K M .Graphite ablation in high pressure environment[R].AIAA 68-1 153 |
| [9] | Xiao Y M;He H Q;Cai T M.Numerical analysis on ablation mechanism of carbon-carbon material during reentry[A].Sacramento,US,1991:97-99. |
| [10] | Han JC.;Du SY.;He XD. .OXIDATION AND ABLATION OF 3D CARBON-CARBON COMPOSITE AT UP TO 3000-DEGREES-C[J].Carbon: An International Journal Sponsored by the American Carbon Society,1995(4):473-478. |
| [11] | Y. I. Dimitrienko I. D. Dimitrienko .Effect of thermomechanical erosion on heterogeneous combustion of composite materials in high-speed flows[J].Combustion and Flame,2000(3):211-226. |
| [12] | Savage G.Carbon-Carbon Composites[M].London:Chapman &Hall and New York:Glasgow,1992:225-229. |
| [13] | Bundy FP.;Weathers MS.;Hemley RJ.;Mao HK.;Goncharov AF.;Bassett WA. .THE PRESSURE-TEMPERATURE PHASE AND TRANSFORMATION DIAGRAM FOR CARBON - UPDATED THROUGH 1994 [Review][J].Carbon: An International Journal Sponsored by the American Carbon Society,1996(2):141-153. |
| [14] | 崔红,苏君明,李瑞珍,李贺军,康沫狂.添加难熔金属碳化物提高C/C复合材料抗烧蚀性能的研究[J].西北工业大学学报,2000(04):669-673. |
| [15] | 王俊山,李仲平,敖明,许正辉,刘朗,胡子君,彭维周.掺杂难熔金属碳化物对炭/炭复合材料烧蚀微观结构的影响[J].新型炭材料,2005(02):97-102. |
| [16] | 王俊山,李仲平,敖明,许正辉,刘朗,胡子君,彭维周.掺杂难熔金属碳化物对炭/炭复合材料烧蚀机理的影响[J].新型炭材料,2006(01):9-13. |
| [17] | Pacault A.The kinetics of graphitization[A].,1971:107-132. |
| [18] | Guigon M;Oberlin A;Desarmot G .Microtexture and struc-.ture of some high tensile strength,PAN-base carbon fiber[J].Fiber Science and Technology,1984,20:55-72. |
| [19] | Zimmer J E;White J L .Disclination structures in the carbonaceous mesophase[J].Adv in Liquid Crystal,1982,5:157-163. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%