利用高功率CO2连续激光照射C2H2,使之热解,成功制备了中空壳状碳纳米颗粒(CNSs),为增强其分散性,用王水对所制备的CNSs进行表面处理.利用TEM、XRD、FTIR以及Zeta电位测量等技术对CNSs和经化学处理后的碳纳米颗粒(T-CNSs)进行了对比分析.结果表明:CNSs壳层内碳原子呈石墨状规则排列;T-CNSs表面带有含氧的亲水官能团,使其很容易分散;化学处理没有改变CNSs的结构.

参考文献

[1] Kroto H W;Heath J R;O' Brien S C et al.C60:Buckminsterfullerene[J].Nature,1985,318:162.
[2] Iijima S .Helical microtubules of graphitic carbon[J].Nature,1991,354:56-58.
[3] 邱介山,孙玉峰,周颖,孙天军,李杞秀.淀粉基碳包覆铁纳米胶囊的合成及其磁学性能[J].新型炭材料,2006(03):202-205.
[4] 吴卫泽,朱珍平,刘振宇.Fe/C复合纳米材料的制备研究[J].新型炭材料,2002(01):4-9.
[5] de Heer W A;Urgate D .Carbon onions produced by heat treatment of carbon soot and their relation to the 217.5 nm interstellar absorption feature[J].Chemical Physics Letters,1993,207:480-486.
[6] Urgate D .Curing and closure of graphitic networks under electron beam irradiation[J].Nature,1992,359(6397):707-709.
[7] Vader Wal R L;Choi M Y .Pulsed laser heating of soot:morphological changes[J].Carbon,1999,37:23-30.
[8] 谢永美,唐小海,何俊,成明,郑开波,张勇.具有优异淋巴示踪特性的纳米炭混悬液的制备[J].新型炭材料,2006(03):259-262.
[9] Shim J W;Park S J;Ryu S K .Effect of modification with HNO3 and NaOH on metal adsorption by pitch-based activated carbon fiber[J].Carbon,2001,39:1635-1642.
[10] 晋卫军,孙旭峰,王煜.碳纳米管溶解性及其化学修饰[J].新型炭材料,2004(04):312-318.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%