利用动态TGA分析和Coats-Redfern模型研究了预氧化聚碳硅烷(PCS)纤维的热分解动力学,用IR、XRD、SEM和HRTEM等研究了其热分解过程与机理.结果表明,预氧化PCS纤维热分解过程为一级反应,表观活化能为19.826kJ/mol;在初始分解阶段,主要为小分子PCS逸出,≡Si-H键之间以及≡Si-H与≡Si-CH3键发生了脱氢、脱CH4反应,从而导致交联程度的增加;随热分解温度进一步提高,分子的有机侧链急剧热解,分解产物从有机物转变为存在部分微晶的无机结构;热分解温度继续提高,纤维无机化结构进一步完善,β-SiC晶粒尺寸增加,纤维中出现自由碳;1 250℃以上,β-SiC晶粒急剧长大,晶粒尺寸增加导致SiC纤维的力学性能下降.
参考文献
| [1] | Johnson D W;Evans A G;Goettler R W.Ceramic Fibers and Coatings:Advanced Materials for the Twenty-First Century[M].Publication NMAB～494,National Academy Press,Washington D C,1998:1-49. |
| [2] | 王其坤,胡海峰,简科,陈朝辉,郑文伟,马青松.先驱体转化法制备2D Cf/SiC-Cu复合材料及其性能[J].新型炭材料,2006(02):151-155. |
| [3] | 黄剑锋,李贺军,熊信柏,曾燮榕,李克智,付业伟,黄敏.炭/炭复合材料高温抗氧化涂层的研究进展[J].新型炭材料,2005(04):373-379. |
| [4] | 刘振宇,郑经堂,王茂章,张碧江.超耐环境性的碳化硅[J].新型炭材料,2000(02):75-79,74. |
| [5] | Yajima S;Hayasgi J;Iimura M.Synthesis of continous silicon carbide fiber with high tensile strength and high Young's Modulus[J].Journal of Materials Science,1978(13):2569-2576. |
| [6] | Yajima S;Hayasgi J;Omori M et al.Development of a SiC fibre with high tensile strength[J].Nature,1976,261:683-685. |
| [7] | Hasegawa Y;Okamura K.Synthesis of continous silicon carbide fibre,part 3:Pyrolysis of polycarbosilane and structure of the products[J].Journal of Materials Science,1983(18):3633-3648. |
| [8] | Ly H Q;Taylor R;Day R J .Conversion of polycarbosilane(PCS) to SiC-based ceramic:Part Ⅱ,pyrolysis and characterization[J].Journal of Materials Science,2001,36:4045-4057. |
| [9] | Coats A W;Redfem J P .Kinetic parameters from thermo-gravimetric data[J].Nature,1964,201:68-69. |
| [10] | 王应德;冯春祥;宋永才.碳化硅纤维连续化工艺研究[J].宇航材料工艺,1997(02):21-25. |
| [11] | Yajima S;Hayasgi J;Omori M et al.Development of a SiC fibre with high tensile strength[J].Nature,1976,261:683-685. |
| [12] | 张利珍,吕春祥,吕永根,吴刚平,贺福.聚丙烯腈纤维在预氧化过程中的结构和热性能转变[J].新型炭材料,2005(02):144-150. |
| [13] | 武向阳,靳国强,郭向云.溶胶-凝胶中Fe催化剂用量对β-SiC堆积缺陷和形貌的影响[J].新型炭材料,2005(04):324-328. |
| [14] | Man T;Hecht N L;Cullum M C et al.Thermal stability of SiC fibers (Nicalon)[J].Journal of Materials Science,1984,19(04):1191-1201. |
| [15] | Clark T J;Arons R M;Stamatoff J B et al.Thermal degradation of nicalon SiC fiber[J].Ceramic Engineering & Science Proceedings,1985,6(7-8):576-578. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%