将不同质量分数的碳纳米管和环氧树脂充分混合,制成复合吸波涂料并涂覆在铝板上制成吸波涂层.采用TEM对碳纳米管的形貌进行观察.使用反射率扫频测量系统HP8757E标量网络分析仪检测复合材料的吸波性能.结果表明,复合材料在2 GHz～18 GHz均有良好的吸波性能.碳纳米管加载质量分数为8 %和10 %时,复合材料吸波性能最佳.8 %碳纳米管加载量,峰值最大,达到～22.55 dB,波峰出现在12.32 GHz,带宽分别为2.56 GHz(R< -8 dB)和4.00 GHz(R< -5 dB).10 %碳纳米管添加量,带宽最大,分别达到2.80 GHz(R< -8 dB)和7.00 GHz (R< -5 dB),波峰出现在13.67 GHz,峰值为-14.59 dB.
参考文献
| [1] | Sumio Iijima .Helical Microtubules of Graphitic Carbon[J].Nature,1991,354:56-58. |
| [2] | 李峰,白朔,成会明.纳米碳管[J].新型炭材料,2000(03):79-80. |
| [3] | 曹宗良,王健农,丁冬雁,戴杰华,余帆.化学气相沉积法快速生长定向纳米碳管[J].新型炭材料,2003(01):48-52. |
| [4] | 刘畅,成会明.电弧放电法制备纳米碳管[J].新型炭材料,2001(01):67-71. |
| [5] | 潘春旭,Liming Yuan,Kozo Saito.扩散火焰合成碳纳米管研究[J].新型炭材料,2001(03):24-27. |
| [6] | FALVO M. R.;CLARY G. J.;TAYLOR R. M.;CHI V.;BROOKS F. P.;WASHBURN S.;SUPERFINE R. .BENDING AND BUCKLING OF CARBON NANOTUBES UNDER LARGE STRAIN[J].Nature,1997(6651):582-584. |
| [7] | Salvetat J.-P.;Thomson N.H.;Kulik A.J.;Forro L.;Benoit W.;Zuppiroli L.;Bonard J.-M. .Mechanical properties of carbon nanotubes[J].Applied physics, A. Materials science & processing,1999(3):255-260. |
| [8] | Demczyk BG.;Wang YM.;Cumings J.;Hetman M.;Han W.;Zettl A.;Ritchie RO. .Direct mechanical measurement of the tensile strength and elastic modulus of multiwalled carbon nanotubes[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):173-178. |
| [9] | Berber S.;Tomanek D.;Kwon YK. .Unusually high thermal conductivity of carbon nanotubes[J].Physical review letters,2000(20):4613-4616. |
| [10] | Ebbesen T W;Lezec H J;Hiura H et al.Electrical conductivity of individual carbon[J].Nature,1996,382:54-56. |
| [11] | Tang Z K;Zhang Lingyun;Wang N et al.Superconductivity in 4 Angstrom single-walled carbon nanotubes[J].Science,2001,292:3462-3465. |
| [12] | 沈曾民,赵东林.镀镍碳纳米管的微波吸收性能研究[J].新型炭材料,2001(01):1-4. |
| [13] | 曹茂盛,高正娟,朱静.CNTs/Polyester复合材料的微波吸收特性研究[J].材料工程,2003(02):34-36. |
| [14] | 杨杰,沈曾民,熊涛.聚苯胺原位包覆碳纳米管材料的制备及性能[J].新型炭材料,2003(02):95-100. |
| [15] | 赵稼祥.碳纤维及其复合材料的新进展[J].新型炭材料,1991(03):21. |
| [16] | 沈曾民,戈敏,赵东林.螺旋形炭纤维的吸波性能[J].新型炭材料,2005(04):289-293. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%