采用表面压-分子面积(π-A)等温曲线和紫外-可见吸收谱的方法研究了一种新型喹吖啶酮衍生物材料LB膜的制备及其光谱特性.实验表明,这种新型喹吖啶酮衍生物能够在水面上形成稳定的单分子膜,它与花生酸(AA)混合后不仅可以形成很好的单分子膜,而且可以较好地转移到固体基片上制备成LB膜多层膜.这种新型喹吖啶酮衍生物LB膜的紫外-可见吸收谱的吸收峰位较稀溶液发生了红移,这是由极性溶剂分子与其相互作用的结果.它在溶液和LB膜中都是以单体的形式存在.
参考文献
[1] | Zasadzinski J A;Viswanathan R;Madsen L et al.Langmuir-Blodgett films[J].Science,1994,263:1726-1733. |
[2] | Roberts G.Langmuir-Blodgett films[M].New York:Plenum Press,1990:20-35. |
[3] | 董声雄 .LB累积层膜的气体传质研究[J].福州大学学报,1993,21:88-92. |
[4] | Matsuo H.;Kuniyoshi S. .Evanescent wave optical fiber sensor using adsorption LB films[J].Synthetic Metals,2000(1/3):37-39. |
[5] | Wang J.;Wang HS.;Fu LS.;Liu FY.;Zhang HJ. .Luminescence properties of LB films based on heteropolytungstate of rare earth[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2003(1):83-86. |
[6] | Schrader Sigurd;Zauls Vismants;Dietzel Birgit et al.Linear and nonlinear optical properties of Langmuir-Blodgett multilayers from chromophore-containing maleic acid anhy-dride polymers[J].Materials Science and Engineering C,1999,8-9:527-537. |
[7] | Labana S S;Labana L L .Quinacridones[J].Chemical Reviews,1967,67:1-18. |
[8] | Jabbour GE;Kawabe Y;Shaheen SE;Wang JF;Morrell MM;Kippelen B;Peyghambarian N .Highly efficient and bright organic electroluminescent devices with an aluminum cathode[J].Applied physics letters,1997(13):1762-1764. |
[9] | Jung Yohn Cho;Ho Jung Chang .Preparation and Characterization of Organic Light Emitting Devices Using QD Dopant[J].Materials Science Forum,2004(Pt.2):1021-1024. |
[10] | Pei-Hua Liu;He Tian;Chen-Pin Chang .Luminescence properties of novel soluble quinacridones[J].Journal of Photochemistry and Photobiology, A. Chemistry,2000(2/3):99-104. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%