采用了一种新颖的改性(Fenton处理)PVDF基体材料的方法,以提高膜的润湿性和耐污染性,并对改性机理做了探讨.结果表明,经Fenton处理后制得的膜亲水性得到了提高,纯水通量由34.6 L/(m2·h)提高到52.3 L/(m2.h),膜表面水接触角由75°降为62.5°,黏附功由91.64 mN/m提高到106.42 mN/m.同时,膜的截留性能也稍有上升,膜的Ji/J0由48.8%提高到69.3%;红外图谱进一步表明,经改性后的膜材料内部接上了丙烯酸(AAc)单体.
参考文献
| [1] | Oshina K H .The use of a microporons poly vinyliden fluoride membrane filter to separate contaminating viral particles from biologically important proteins[J].I/O Logicals,1996,24(02):137-145. |
| [2] | Jian K.;Pintauro PN. .ASYMMETRIC PVDF HOLLOW-FIBER MEMBRANES FOR ORGANIC/WATER PERVAPORATION SEPARATIONS[J].Journal of Membrane Science,1997(1):41-53. |
| [3] | Li K.;Kong J.F.;Wang Dongliang .Tailor-Made Asymmetric PVDF Hollow Fibers for Soluble Gas Removal[J].AIChE Journal,1999(6):1211-1219. |
| [4] | Chahot S;Roy C;Chowdhuryl G et al.Development of PVDF hollow fibermembranes for the treatment of water/organic vapor mixtures[J].Journal of Applied Polymer Science,1997,65:1263-1270. |
| [5] | Xu Zhen-Liang;Loh Kai-Chee;Lim Bee Chun;Chung Tai-Shung .Polymeric asymmetric membranes made from polyetherimide/polybenzimidazole/poly(ethylene glycol) (PEI/PBI/PEG) for oil-surfactant-water separation[J].Journal of Membrane Science,1999(1):41-53. |
| [6] | Lindau J.;Jonsson A.-S. .Adsorptive fouling of modified and unmodified commercial polymeric ultrafiltration membranes[J].Journal of Membrane Science,1999(1):65-76. |
| [7] | Faibish RS.;Cohen Y. .Fouling and rejection behavior of ceramic and polymer-modified ceramic membranes for ultrafiltration of oil-in-water emulsions and microemulsions[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2001(1/2):27-40. |
| [8] | 张玉忠;郑领英;高从堦.液体分离膜技术及应用[M].北京:化学工业出版社,2004:38-39. |
| [9] | 王庐岩,钱英,刘淑秀,叶晓.聚偏氟乙烯分离膜改性研究进展[J].膜科学与技术,2002(05):52-57. |
| [10] | 雷乐成;汪大翚.水处理高级氧化技术[M].北京:化学工业出版社,2001:58-59. |
| [11] | 董声华,郑领英.不同标准物表征超滤膜截留性能的比较[J].水处理技术,1993(06):319. |
| [12] | 龚琦,杜邵龙,董声雄.小截留分子量共混超滤膜的研究（Ⅲ）--PVDF与PVAc共混超滤膜的后处理及化学稳定性比较[J].福州大学学报(自然科学版),2002(06):887-890. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%