以FeCl2为还原剂,采用模板和化学镀相结合的方法制备Fe3O4/PSF磁性复合超滤膜,对所制膜的表面形貌、内部结构和孔径大小等性质进行表征,随后进行溶菌酶截留实验,并对截留机理进行分析.扫描电镜(SEM)观察可知,粒子主要沉积在复合膜的孔道中;X射线衍射(XRD)分析可知,沉积粒子主要为Fe3O4,粒径为6.99 nm;液液界面法测得,复合超滤膜的平均孔径从无磁场下的9.36 nm减小到0.8 T磁场下的8.54 nm;在外加磁场下,复合超滤膜对不带电的溶菌酶截留率增大,对带电的溶菌酶截留率减小.经过分析认为,复合超滤膜在磁场下的超滤机理,主要是磁场诱导效应和磁致伸缩效应,并且前者的作用大于后者.
参考文献
| [1] | Tansel B;Regula J;Shalewitz R .Treatment of fuel oil and crude oil contaminate waters by ultrafiltration membranes[J].Desalination,1995,102(05):301-311. |
| [2] | Ghosh R.;Cui ZF. .Protein purification by ultrafiltration with pre-treated membrane[J].Journal of Membrane Science,2000(1):47-53. |
| [3] | A.Bottino;G.Capannelli;V.D'Asti;P.Piaggio .Preparation and properties of novel organic-inorganic porous membranes[J].Separation and Purification Technology,2001(0):269-275. |
| [4] | Lu Yan;Yu Shui Li .Effect of nano-sized Al2O3-particle addition on PVDF ultrafiltration membranes performance[J].Membr Sci Technol,2006,276(04):162-167. |
| [5] | Han P;Yahui H;Yang W;Linlin L .Preparation of polysulfone-Fe3O4 composite ultrafiltration membrane and its behavior in magnetic field[J].Journal of Membrane Science,2006(1/2):9-16. |
| [6] | 杜军,吴玲,陶长元,孙才新.纳米Fe3O4/PVDF磁性复合膜的原位制备及表征[J].物理化学学报,2004(06):598-601. |
| [7] | 王明旭,魏志强,李年春,赵学福,闫鹏勋.镍纳米粉的粒度研究[J].材料导报,2006(z1):166-168. |
| [8] | 王湛;周翀.膜分离技术基础[M].北京:化学工业出版社,2006:220-221. |
| [9] | 诸爱士,林贤诉,高兴.液-液置换法测试超滤膜孔径及其分布的研究[J].浙江科技学院学报,2004(04):239-243. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%