以二乙二醇和PEG400为混合稀释荆,以乙烯摩尔分数为38%的乙烯-乙烯醇共聚物(EVOH38)为原料,用热致相分离法制备亲水性微孔膜.微孔膜形态分析表明当二乙二醇与PEG400质量比为2:8,冷却方式为冰水淬冷时,得到的微孔断面为双连续网状结构.测定了EVOH38/二乙二醇/PEG400体系不同稀释剂组成的雾点和结晶温度,研究了稀释剂组成、冷却方式对微孔膜断面微观形态的影响,并且表征了所得平板膜的拉伸性能和纯水通量,结果表明该膜具有一定力学性能,较好水通量.
参考文献
[1] | Liu B.;Yang YL.;Du QG. .The phase diagrams of mixtures of EVAL and PEG in relation to membrane formation[J].Journal of Membrane Science,2000(1):81-92. |
[2] | 杨健,王晓琳.聚丙烯微孔膜亲水化研究进展[J].高分子材料科学与工程,2006(04):6-9,14. |
[3] | Hideto Matsuyama;Tomofumi Iwatani;Yoshiro Kitamura .Formation of Porous Poly(ethylene-co-vinyl alcohol) Membrane via Thermally Induced Phase Separation[J].Journal of Applied Polymer Science,2001(13):2449-2455. |
[4] | Castro A J .Method for making microporous products[P].US Pat:4247498,1981-01-27. |
[5] | 郭行蓬,柳波,葛昌杰,杜强国,杨玉良.热致相分离法制备微孔EVAL中空纤维膜的探索[J].功能高分子学报,2001(01):23-26. |
[6] | 殷杰,钟伟,杜强国,杨玉良.热致相分离法EVOH微孔膜的制备和形态[J].膜科学与技术,2004(06):10-14. |
[7] | Hideto Matsuyama;Tomofumi Iwatani;Yoshiro Kitamura .Solute Rejection by Poly(ethylene-co-vinyl alcohol) Membrane Prepared by Thermally Induced Phase Separation[J].Journal of Applied Polymer Science,2001(13):2456-2463. |
[8] | Hideto Matsuyama;Kiyotaka Kobayashi;Taisuke Maki;Masaaki Tearamoto;Hitoshi Tsuruta .Effect of the Ethylene Content of Poly(ethylene-co-vinyl alcohol) on the Formation of Microporous Membranes via Thermally Induced Phase Separation[J].Journal of Applied Polymer Science,2001(10):2583-2589. |
[9] | Shang MX.;Matsuyama H.;Maki T.;Teramoto M.;Lloyd DR. .Preparation and characterization of poly(ethylene-co-vinyl alcohol) membranes via thermally induced liquid-liquid phase separation[J].Journal of Applied Polymer Science,2003(5):853-860. |
[10] | 谢林锋,陆晓峰,李磊,沈飞,李文俊.热致相分离法平片式聚(乙烯-乙烯醇)微孔膜的制备和表征[J].净水技术,2005(03):1-6. |
[11] | 朱晓伟,陆晓峰,侯铮迟,段伟,卞晓楷,施柳青.热致相分离法制备平片式EVOH微孔膜研究[J].膜科学与技术,2009(01):41-46. |
[12] | 吕睿 .热致相分离法制备EVOH微孔膜的基础研究[D].复旦大学,2006. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%