采用力学性能试验、TEM及SEM研究了15CrMnMoV钢板中的内生复合效应.结果表明:将15CrMnMoV钢板冷轧而制备的内生复合钢板,其σ02在1500~1660MPa之间,KIc在98.6~110.7MPa·m1/2之间,KISCC在75~95MPa·m1/2之间,表现出了超高强韧性;内生复合效应的本质在于塑性变形使得15CrMnMoV钢板成为(100)织构取向带镶嵌于(111)织构取向带中的复合结构,弱界面为(100)/(100)晶间界面,裂纹扩展过程中弱界面的分层现象使得其断裂韧度大幅度提高.

参考文献

[1] 温仲元.金属基复合材料[M].北京:国防工业出版社,1982:36-47.
[2] 陈石卿.断裂热力学[M].北京:国防工业出版社,1984:192-194.
[3] Coox J;Gordon J E .A mechanism for the control of crack propagation in all brittle systems[J].Proceedings of the Royal Society of London,1964,A282(1391):508-519.
[4] Rao K T V;Yu Weikang;Ritchie R O .Cryogenic toughness of commercial aluminum-lithium alloys:role of delamination toughening[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1989,20(03):485-497.
[5] Spitzing W A .Strength and electrical conductivity of a deformation-processes Cu5Pct-Nb composite[J].Metallurgical and Materials Transactions,1993,24(01):7-14.
[6] Liu C D;Bassim M N .Dislocation substructure evolution in torsion of pour copper[J].Metallurgical and Materials Transactions,1993,24(02):361-372.
[7] Hushes D A;Hansen N .Microstructure evolution in nickel during rolling from intermediate to large strain[J].Metallurgical and Materials Transactions,1993,24(09):2021-2037.
[8] Jing Tianfu;Zhang Jingwu;Fu Wantang;Gao Ming .High performance steel plates with micro-laminated layer structure produced by plastic deformation[J].Journal of Materials Science Letters,1997(6):485-489.
[9] 荆天辅;王明智 等.15CrMnMoV钢分层致韧效应的研究[J].钢铁,1992,27(02):44-48.
[10] 高明;荆天辅 等.形变时效改善超高强度钢应力腐蚀抗力的研究[J].机械工程学报,1993,29(04):29-34.
[11] 冷轧压下量及时效温度对内生 复合钢板弱界面结合强度的影响[J].热加工工艺,2000(01):7-9.
[12] 蔡大勇,张春玲,荆天辅.多道次冷轧法制备内生复合钢板[J].特殊钢,2000(01):50-52.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%