研究了铝热-离心法制备的复合钢管中不锈钢内衬层的显微结构以及固溶处理对不锈钢层的显微结构及力学性能的影响.结果表明,不锈钢内衬层主要由奥氏体枝晶组成,枝晶间分布着一薄层铁素体.铁素体区内有AlNi金属问化合物析出.奥氏体和铁素体的相界面上有σ相析出.1000℃固溶处理可消除缓慢冷却过程中在不锈钢中形成的σ相和AlNi析出相,显著提高不锈钢的塑性,不锈钢内衬层的伸长率由处理前的8%提高到处理后的21%.
参考文献
[1] | Merzhanov A G.Self-Propagating High-Temperature Synthesis:Twenty Years of Search and Findings[A].New York:VCH Publishers,1990:1-53. |
[2] | Odawara O .Long ceramic-lined pipes produced by a centrifugal-thermit process[J].Journal of American Ceramic Society,73(03):629-633. |
[3] | 段辉平 .离心-铝热法制备不锈钢内衬复合钢管的研究[D].北京科技大学,1996. |
[4] | DUAN Hui-ping;Yin Sheng;Liu Mu;Lai Hoyi .Stainless steel lined composite pipe produced by centrifugal SHS process[J].Journal of Materials Science Letters,1996,15:1060-1061. |
[5] | 席文君;殷声;赖和怡 .自蔓延离心法制备的不锈钢内衬复合钢管的力学性能[J].金属学报,1999,35(02):137-141. |
[6] | Xi Wenjun;Yin Sheng;Lai Hoyi .Stainless steel lined composite pipe prepared by centrifugal-SHS process[J].Journal of Materials Science,2000,35(02):45-49. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%