利用内氧化法制备了Cu-Al2O3弥散强化铜合金,并对其挤压态、冷拉态、退火态棒材进行了性能测试和显微组织结构分析.结果表明:挤压后的棒材经65%和90%的变形量冷拉拔后,存在明显的加工纤维组织,σb分别达468和495MPa,相对电导率分别为90%和89%IACS;1030℃×0.5h高温退火后再结晶现象并不明显,仍能保持较高的强度;且变形量越大,高温退火后强度下降越小;合金的拉伸断口表现为韧性与脆性的混合型断裂.
参考文献
| [1] | Nadkarni A V.Dispersion strengthened copper properties and application[A].The Metallurgical of AIME Warrendale,PA,1984:77. |
| [2] | Joanna Groza .Heat-resistant dispersion-strengthened copper alloys[J].Journal of Materials Engineering and Performance,1992,1(01):113-121. |
| [3] | 闵光辉;宋立;于化顺 等.高强度导电铜基复合材料[J].功能材料,1997,28(04):342-355. |
| [4] | 张毅,周延春.Ti3SiC2弥散强化Cu：一种新的弥散强化铜合金[J].金属学报,2000(06):662-666. |
| [5] | 申玉田;崔春翔;孟凡斌;吴人洁 .高强度高导电率Cu-Al2O3复合材料的制备[J].金属学报,1999,35(08):888-892. |
| [6] | 王碧文.铜及铜合金研究方向[C].中国有色金属学会第三届学术会议论文集,1997:310～316. |
| [7] | Broyles S E;Anderson K R;Groza J R .Creep deformation of dispersion strengthening copper[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1996,27(05):1217-1227. |
| [8] | Synk J E;Vedula K .Structure and mechanical behaviour of powder processed dispersion strengthened copper[J].材料科学与工艺(英文版),1987,3(01):72-75. |
| [9] | Ashby M F;Smith G C .Structure in internally oxidated copper alloys[J].Journal of the Institute of Metals,1963,91:182-187. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%