采用火焰加热方式对6005A铝合金型材焊接变形进行矫正.研究了不同加热温度对焊接接头拉伸强度、硬度及微观组织结构的影响.实验结果表明,当火焰加热温度低于175℃时,焊接接头的拉伸强度、硬度未降低,热影响区内软化区的显微组织未发生明显变化.当加热温度超过200℃时,焊接接头的硬度发生较明显降低现象,拉伸断裂处随着加热温度的升高向基材方向移动,软化区显微组织粗化;软化区材料性能下降的原因是在焊接及后续的火焰矫形热循环过程中过热导致该区晶粒粗大.
参考文献
| [1] | Tsai C L;Park S C;Cheng W T .Welding distortion of a thin-plate panel structure[J].Welding Journal,1999,78:156-165. |
| [2] | Bae B Y;Na S J .An analysis of thermal stress and distortion in bead-on-plate welding using laminated isotropic plate theory[J].Journal of Materials Processing Technology,1996,57:337-344. |
| [3] | 拉达伊D;熊第京.焊接热效应-温度场、残余应力、变形[M].北京:机械工业出版社,1997 |
| [4] | Labanov L M.Heat abstracting paste reduces distortions[J].Welding & Metal Fabrication,1982(03):65-70. |
| [5] | Tian Xitang .Prevention of hot cracking by trailing cooling along the weld[J].哈尔滨工业大学学报(英文版),1994,1(01):59-61. |
| [6] | Schmidt C G;Shocxey D A .Reduction of residual stresses in weldments with explosive treatments[J].Welding Journal,1992,71(12):443-447. |
| [7] | Michaleris P;Sun X .Finite element analysis of thermal tensioning techniques mitigating weld bulking distortion[J].Welding Journal,1997,76:451-457. |
| [8] | 徐文立 .随焊锤击控制铝合金薄板焊接应力变形及接头质量的研究[D].哈尔滨工业大学,2001. |
| [9] | 水野政夫;蓑田和之;阪口章;许慧姿.铝及其合金的焊接[M].北京:冶金工业出版社,1985 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%