采用纳米Ti(C,N)粉末制备Ti(C,N)基金属陶瓷,研究了纳米粉末对金属陶瓷组织及性能的影响.结果表明,粉末冶金过程中,纳米Ti(C,N)粉末易于在粘结相中扩散与溶解及沿晶界分布,降低了硬质相在粘结相中的溶解度,抑制了晶粒长大,提高了材料的红硬性能.抗弯强度与晶粒尺寸满足于Hall-Petch公式,5wt%～10wt%的纳米粉末加入量可使金属陶瓷的抗弯强度和切削性能得到较大的提高,但硬度变化不大.切削磨损主要表现为磨粒磨损和轻微的粘着磨损,磨痕细小均匀.
参考文献
| [1] | Ettmayer P;Lengatierw .The story of cermets[J].Powder Metallurgy International,1989,21(02):37-48. |
| [2] | Chen Limin;Lengauer Walter .Dreyer Klaus. Advances in modern nitrogen-containing hardmetals and cermets[J].International Journal of Refractory Metals and Hard Materials,1999,18(02):153-161. |
| [3] | Nishimura T;Murayama K;Kitada T;Takashima Y .Some properties of cermet sintered in nitrogen gas[J].International Journal of Refractory Metals and Hard Materials,1985,35:31-33. |
| [4] | P. Lindahl;A. E. Rosen;P. Gustafson .Effect of pre-alloyed raw materials on the microstructure of a (Ti, W) (C, N)-Co cermet[J].International Journal of Refractory Metals & Hard Materials,2000(6):273-279. |
| [5] | Zackrisson J;Rolander U;Weinl G et al.Microstructure of the surface zone in a heat-treated cermet material[J].International Journal of Refractory Metals and Hard Materials,1998,16:315-322. |
| [6] | Wahi P R;Ilschner B .Fracture behavior of composites based on Al2O3-TiC[J].Journal of Science,1980,15:875-885. |
| [7] | Shobu K;Watanable T .Frictional properties of sintered TiN-TiB2 and Ti(C,N)-TiB2 ceramics at high temperature[J].Journal of the American Ceramic Society,1987,70(05):103-104. |
| [8] | 许育东,刘宁,曾庆梅,李华,石敏.纳米TiN改性金属陶瓷刀具的磨损性能[J].硬质合金,2001(03):142-145. |
| [9] | 陈华辉;邓海金;李明;林小松.现代复合材料[M].北京:中国物资出版社,1998:303. |
| [10] | 周敬恩.金志浩非金属工程材料[M].西安:西安交通大学出版社,1987 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%