等离子喷涂Fe基非晶合金涂层的耐磨性能较好,其磨损是一个缓慢逐层磨削过程;经晶化处理后,涂层硬度升高但韧性下降,涂层耐磨性能变差,当涂层完全晶化并基本上由Fe-B硬质化合物相组成时,耐磨性最差,其磨损是一个涂层表面层在外加载荷作用下不断被压裂而脱落并被碾碎成微粒的过程.非晶合金涂层在0.5mol H2SO4溶液和在3.5%NaCl溶液中具有钝化作用,随涂层厚度的增加,钝化区加宽,维钝电流密度降低并保持在较低值,涂层的抗腐蚀性能提高.
参考文献
| [1] | 王一禾;杨膺善.非晶态合金[M].北京:冶金工业出版社,1989 |
| [2] | Kishitake K;Era H;Otsubo F .Characterization of plasma sprayed Fe-17Cr-38Mo-4C amorphous coatings crystallizing at extremely high temperature[J].Journal of Thermal Spray Technology,1996,5(05):283-288. |
| [3] | Sanjay Sampath .Microstructural characteristics of plasma spray consolidated amorphous powders[J].Materials Science and Engineering,1993,A167:1. |
| [4] | Dent AH.;McCartney DG.;Harris SJ.;Horlock AJ. .Microstructural characterisation of a Ni-Cr-B-C based alloy coating produced by high velocity oxy-fuel thermal spraying[J].Surface & Coatings Technology,2001(2/3):244-250. |
| [5] | 向兴华,刘下义,朱晖朝.Fe基非晶合金涂层的等离子喷涂制备工艺研究[J].材料工程,2002(02):10-12,插2. |
| [6] | 穆晓冬,向兴华,刘正义.Fe基非晶合金涂层在晶化过程中的硬度与组织变化[J].材料工程,2003(05):33-36. |
| [7] | 孙秋霞.材料腐蚀与防护[M].北京:冶金工业出版社,2001 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%