制备了添加少量B2O3和P2O5后的FeO-Fe2O3-CaO-SiO2体系铁磁微晶玻璃,并对不同热处理条件下获得的样品进行了微观结构分析和XRD分析.实验结果表明,微晶玻璃的主晶相为磁铁矿,磁铁矿成核容易,在玻璃冷却过程中就能够形成大量的磁铁矿晶核;次晶相为硅灰石,核化势垒较大,它在热处理中形成晶核.不经过核化处理在1000℃晶化2h能够获得较理想的磁铁矿主晶相和硅灰石次晶相均匀致密分布的微观组织.
参考文献
| [1] | Ohura K;Ikenaga M;Nakamura T et al.A heat-gearating bioactive glass-ceramic for hyperthermia[J].Journal of Applied Biomaterials,1991,2:755-761. |
| [2] | Ebisawa Y;Kokubo T;Ohura K et al.Bioactivity of CaO-SiO2-based glasses:in vitro evaluation[J].Journal of Materials Science:Materials in Medicine,1992,4:225-232. |
| [3] | Ebisawa Y.;Kokubo T.;Ohura K.;Nakamura T.;Miyaji F. .BIOACTIVITY OF FERRIMAGNETIC GLASS-CERAMICS IN THE SYSTEM FEO-FE2O3-CAO-SIO2[J].Biomaterials,1997(19):1277-1284. |
| [4] | 陈建华,杨南如.钙铁硅铁磁体微晶玻璃晶化与核化的研究[J].硅酸盐学报,2001(03):238-244. |
| [5] | 吴知方,黄文,周萘,茅波,林伟.磁热效应的铁钙磷酸盐生物微晶玻璃研制[J].建筑材料学报,2001(02):154-158. |
| [6] | Tadashi Kokubo .Apatite formation on surfaces of ceramics, metals and polymers in body environment[J].Acta materialia,1998(7):2519-2527. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%