采用电沉积-烧结方法制备Co3O4锂离子电池负极.X射线衍射XRD分析表明,电沉积的物质是Co(OH)2相,300℃烧结后均转变为Co3O4相.扫描电镜SEM观察发现获得的Co3O4具有花瓣形貌,其花瓣厚度约20nm.在300℃分别烧结30、45、60min制备的Co3O4组装的Co3O4/Li电池,在充放电循环中的首次嵌锂比容量分别为1361.7、1457.6和1345.0 mAh/g,首次脱锂比容量分别为757.7、905.0和794.8mAh/g,10次循环后,脱锂比容量分别上升到815.5、969.0和890.1mAh/g.
参考文献
[1] | 郭炳琨;徐徽.锂离子电池[M].长沙:中南大学出版社,2002 |
[2] | ChenY;Wang G X;Konstantinov K.Studies of the electrochemical properties of nanosize Co3 O4 oxide as an anode material for lithium-ion batteries[A].Ahn J H,Hahn Y D,Editors:Seoul,South Korea,2003:625-628. |
[3] | PoizotP et al.Nano-sized transition-metal oxides as negative-electrode materials for lithium-ion batteries[J].NATURE,2000,407:496-450. |
[4] | 黄峰,袁正勇,周运鸿,孙聚堂.纳米钴基氧化物锂离子电池负极材料的研究[J].电化学,2002(04):397-403. |
[5] | YuWei-pingWangXiao-ping et al.Oxidation resistant coatings of ZrO2 and ZrO2-Y2O3 deposited by high energy pulse plusma[J].High Temperature Materials and Processes,2000,19(06):435-442. |
[6] | YU Weiping,LI Fan,MENG Lin.ZrO2 and ZrO2-Y2O3 coatings deposited by double pulsed plasma arc[J].科学通报(英文版),2002(03):252-254. |
[7] | 金野英隆 .电析法にょる高温耐食性酸化物皮膜の形成[J].非晶质あつき机能非晶质あっき专门部会例会テキスト,1992,22:8-16. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%