采用球形压痕试验,在高速钢基体上对电弧离子镀工艺沉积制备的(Ti,Nb)N膜层断裂性能进行评价.在600N载荷下,在压痕的周围只产生径向裂纹;统计分析压痕周围产生的裂纹,采用裂纹密度函数β,对膜层的断裂性能进行了分析.结果表明:(Ti,Nb)N均质膜层在显微硬度提高的同时,裂纹密度β增加,膜层的脆性增大,断裂韧度下降.TixNb1-xN梯度膜具有较高膜层显微硬度,仍然具有较好的断裂韧度,预渗氮处理的膜层裂纹密度较小,膜层的断裂韧度最好.采用裂纹密度函数β统计分析,通过对(Ti,Nb)N膜层压痕试验,可以很好的定量和半定量地比较膜层的断裂性能.
参考文献
| [1] | DiaoDF;Kato K;Hokkirigawa K .Fracture mechanisms of ceramic coating in indentation[J].Transactions of the ASME,1994,116:860-869. |
| [2] | OettelH;Wiedemann R .Residual stresses in PVD hard coatings[J].Surface and Coatings Technology,1995,76-77:265-273. |
| [3] | MehrotraPK;QuintoDT .Technique for evaluating mechanical properties of hard coatings[J].Journal of Vacuum Science and Technology A,1985,A3(06):2401-2405. |
| [4] | LawnBR;Vilshaw R Y.Review indentation fracture principles and application[J].Journal of Materials Science,1975(10):1049-1081. |
| [5] | LawsN R;Brockenbrough J .The effect of microcrack systems on the loss of stiffness of brittle solids[J].International Journal of Solids and Structures,1987,23:1247-1268. |
| [6] | 高玉周,陈军,林国强,严立.电弧离子镀（TiNb）N硬质薄膜的成分、结构与硬度[J].大连海事大学学报,2004(01):81-84. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%