利用改变高钒高速钢淬火加热温度和回火温度获得不同残余奥氏体量,研究了残余奥氏体量对硬度、冲击韧性和磨粒磨损性能的影响.结果表明:淬火加热温度升高,残余奥氏体量增加;回火温度升高,残余奥氏体量减少.随残余奥氏体量增加,硬度呈二次曲线状先升高后降低,冲击韧性近似直线升高,磨损量呈二次曲线状先下降后升高.残余奥氏体量为20%～40%(vol%)时,高钒高速钢的硬度高,冲击韧性适中,磨粒磨损耐磨性最好.
参考文献
| [1] | SanoY;Hattori T;Haga M .Characteristics of high carbon high speed steel rolls for hot strip mill[J].ISIJ International,1992,32(11):1194-1201. |
| [2] | KeunChulHwang;Sunghak Lee;Hui Choon Lee .Effects of alloying elements on microstructure and fracture properties of cast high speed steel rolls Part Ⅰ: Microstructural analysis[J].Materials Science and Engineering,1998,A254:282-295. |
| [3] | 徐流杰,魏世忠,龙锐,王守诚.高钒高速钢的磨粒磨损行为研究[J].矿山机械,2003(11):77-79. |
| [4] | GotoT;Matsuda Y;Sakamoto K et al.Basic characteristics and microstructure of high-carbon high speed steel rolls for hot rolling mill[J].ISIJ International,1992,32(11):1184-1189. |
| [5] | 于新泉 .复合轧辊用高速钢显微组织及性能的研究[D].郑州大学,2002. |
| [6] | 龙锐,魏世忠,刘亚民,倪锋,徐流杰.高钒高耐磨合金的组织与性能[J].矿山机械,2001(12):54-56. |
| [7] | 徐流杰,魏世忠,龙锐,倪锋,刘亚民,王守成.高钒高速钢中碳化钒的形态分布研究[J].铸造,2003(11):1069-1073. |
| [8] | 崔忠圻.金属学与热处理[M].北京:机械工业出版社,1996:366. |
| [9] | 田莳;李秀臣;李邦淑.金属物理性能[M].北京:国防工业出版社,1985:137-138. |
| [10] | 郭耕三.高速钢及其热处理[M].北京:机械工业出版社,1985:194. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%