利用预涂NiC-Si复合粉末对TiAl合金进行激光熔覆处理,分析了涂层的显微组织及其形成机理,并讨论了显微组织与预涂合金粉末成分的关系.结果表明:涂层的显微组织由初生块状Ti5Si3相及点状γ-NiCrAl/TiSi共晶组织组成,随着预涂合金粉末中Si含量的增加,涂层中初生Ti5Si3块状相的体积分数增大,显微硬度提高,涂层与基体之间为良好的冶金结合.
参考文献
[1] | Ye, HQ .Recent developments in Ti sub 3 Al and TiAl intermetallics research in China[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,1999(2):289-295. |
[2] | R. Yang;Y. Y. Cui;L. M. Dong;Q. Jia .Alloy development and shell mould casting of gamma TiAl[J].Journal of Materials Processing Technology,2003(2/3):179-188. |
[3] | 刘秀波;余利根;王华明 .γ-TiAl合金激光表面合金化γ-NiCrAl/TiC/Cr7C3复合材料涂层组织与性能[J].稀有金属材料与工程,30(03):224-227. |
[4] | Vasudevan A K;Petrovie J J .A comparative overview of molybdenum disilicide composites[J].Materials Science and Engineering A,1992,155:1-17. |
[5] | Rosenkranz R;Fommeyer G .Microstructure and properties of high melting point intermetallic Ti5 Si3 and TiSi2 compounds[J].Materials Science and Engineering A,1992,152:288-294. |
[6] | Sorin Ignat;Pierre Sallamand;Alexandru Nichici .MoSi_2 laser cladding--elaboration, characterisation and addition of non-stabilized ZrO_2 powder particles[J].Intermetallics,2003(9):931-938. |
[7] | Manna I;Weisheit A;Mordike BL;Dutta Majumdar J .Laser surface alloying of Ti with Si, Al and Si+Al for an improved oxidation resistance[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(1/2):123-134. |
[8] | Wang HM.;Liu YF. .Microstructure and wear resistance of laser clad Ti5Si3/NiTi2 intermetallic composite coating on titanium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):126-132. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%