采用粉末冶金法制备了不同SiCp含量的SiCp/Fe-3Cu-C复合材料,研究了烧结温度、SiCp含量及SiCp表面镀镍对材料组织结构、力学性能和干摩擦磨损性能的影响.结果表明,在1050℃烧结能获得最佳的力学性能,加入0.5wt%-2wt%SiCp使材料的强度略有降低,耐磨性显著增强;烧结铁基合金的磨损机制为擦伤、疲劳磨损、粘着磨损,烧结SiCp/Fe-3Cu-C复合材料主要为擦伤和磨粒磨损;SiCp含量约0.5wt%的复合材料耐磨性最佳,SiCp经镀镍处理后进一步提高其耐磨性,最佳SiCp含量提高到1wt%～1.5wt%.
参考文献
| [1] | Guangwei HAN,Di Feng.Synthesis of SiC/Al Co-Continuous Composite by Spontaneous Melt Infiltration[J].材料科学技术学报(英文版),2000(05):466-470. |
| [2] | Lee Y F;Lee S L;Chuang C L et al.Effects of SiCp reinforcement by electroless copper plating on properties of Cu/SiCp composites[J].Powder Metallurgy,1999,2:147-152. |
| [3] | Tang WM.;Zheng ZX.;Ding HF.;Jin ZH. .A study of the solid state reaction between silicon carbide and iron[J].Materials Chemistry and Physics,2002(3):258-264. |
| [4] | 吴人洁 .金属基复合材料的现状与展望[J].金属学报,1997,33(01):78-84. |
| [5] | 邹正军,刘君武.化学镀法制备SiCp-Ni复合粉体[J].表面技术,2002(05):19-21. |
| [6] | Kalogeropoulou S;Baud L .Relationship between wettability and reactivityin SiC/Fe system[J].Acta Metallurgica Et Materialia,1995,43(03):907-914. |
| [7] | 肖志瑜;李元元;夏伟.SiC颗粒增强的钢基复合材料的快速磨损试验研究[J].润滑与密封,1998(zk):40-43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%