研究了960℃和1000℃固溶处理后,时效对马氏体沉淀硬化不锈钢0Cr15Ni5Cu2Ti微观组织与力学性能影响.结果表明,采用960℃和1000℃固溶处理,在455～460℃时效冲击值出现最低值,断口表现为准解理;强度和硬度在460℃时效出现峰值.主要与组织中细小富铜相共格析出有关.随着时效温度增加,钢中富铜相长大,强度和硬度也随之降低.
参考文献
| [1] | James M. Dahl .Ferrous-base aerospace alloys[J].Advanced Materials & Processes,2000(5):33-36. |
| [2] | Carter C S;Farwick D G et al.Stress corrosion properties of high strength precipitation hardening strainless steel[J].Corrosion Nacf,1971,27(05):190-197. |
| [3] | Habibi H R;Servant C et al.TEM investigation of precipitation phenomena occurring in PH15-5 alloy[J].ACTA METALLURGICA ET MATERIALIA,1993,41(05):1613-1623. |
| [4] | Warren M;Garrsion Jr.Nickel content,fine-scale microstructure and ductile-to-brittle transition temperature of martensitic precipitation strengthened stainless steels[A].ISS,1999:831-842. |
| [5] | Rack H J;David K .The strength and low cycle fatigue behavior of 17-4PH stainless steel[J].Metallurgical and Materials Transactions,1974,23(05):1595-1607. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%