用CO2激光在TC4合金表面熔覆TiC+Ti和TiC+NiCrBSi金属陶瓷涂层,分析了熔覆层的微观组织,测试了熔覆层的干滑动磨损性能.结果表明,在TiC+Ti激光熔覆层中,TiC颗粒全部溶解,熔覆层的组织是在β-Ti基体上分布着TiC树枝晶;在TiC+NiCrBSi激光熔覆层中,TiC颗粒部分溶解,熔覆层的组织是在γ-Ni树枝晶和γ-Ni+M23(CB)6共晶的基体上分布着细小的TiC颗粒和TiC树枝晶.TiC+Ti激光熔覆层的显微硬度在500～700HV之间,质量磨损率约为TC4合金的1/3;TiC+NiCrBSi激光熔覆层的显微硬度在900～1100HV之间,质量磨损率约为TC4合金的1/10.
参考文献
| [1] | Ayers J D .Wear behavior of carbide-injected titanium and aluminum alloys[J].Wear,1984,97:249-266. |
| [2] | Mridha S;Baker T N .Composite laser formation on Ti-6Al-4V surfaces by laser treatment using preplaced SiC powder[J].Surface Engineering,1997,13(03):233-237. |
| [3] | Mehlmann A;Dirnfeld S F;Minkoff I .Laser-melt injection of B4 C on titanium[J].Surface and Coatings Technology,1990,42:275-281. |
| [4] | 陈赤囡.TC9激光熔覆TiN涂层的组织与耐磨性的研究[J].北京航空航天大学学报,1998(03):253. |
| [5] | 李平,邓永瑞.钛合金表面激光熔覆氧化锆陶瓷过渡区的显微组织[J].稀有金属材料与工程,1995(05):17-22. |
| [6] | Molian P A;Hualun L .Laser cladding of Ti-6Al-4V with BN for improved wear performance[J].Wear,1989,130:337-352. |
| [7] | 孙荣禄,杨贤金.激光熔覆原位合成TiC-TiB2/Ni基金属陶瓷涂层的组织和摩擦磨损性能[J].硅酸盐学报,2003(12):1221-1224. |
| [8] | 孙荣禄,刘勇,杨德庄.TC4合金及其表面TiCp/Ni基合金激光熔覆层的摩擦磨损性能[J].摩擦学学报,2003(06):457-462. |
| [9] | Mridha S;Baker T N .Metal matrix composite laser formed by laser processing of commercial purity Ti-SiCp in nitrogen environment[J].Materials Science and Technology,1996,12:595-602. |
| [10] | 张松,张春华,吴维,王茂才.Ti6Al4V表面激光熔覆原位自生TiC颗粒增强钛基复合材料及摩擦磨损性能[J].金属学报,2001(03):315-320. |
| [11] | 武万良,黄文荣,杨德庄,孙荣禄.Ti-6Al-4V合金基体上激光熔覆Ti+TiC粉末的显微组织[J].激光技术,2003(04):307-310. |
| [12] | 刘江龙;邹至荣;苏宝熔.高能束热处理[M].北京:机械工业出版社,1997:144-158. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%