用扫描电镜(SEM)、透射电镜(TEM)并结合图像分析方法研究了分别添加1wt%Mn和1wt%Si对Fe-0.8C共析珠光体钢重度冷轧及退火后显微组织以及渗碳体颗粒长大动力学的影响.结果表明,Mn和Si的加入可明显抑制重度冷轧及退火过程中珠光体渗碳体颗粒的长大过程,并使其球化程度及尺寸分布均匀性增大;锰细化重度冷轧及退火后珠光体钢渗碳体颗粒的作用效果优于硅;三种试验用钢重度冷轧及退火后渗碳体颗粒长大动力学方程分别为:对于Fe-0.8C钢,d=186.4t0.195;对于Fe-1Si-0.8C钢,d=90.5t0.205;对于Fe-1Mn-0.8C钢,d=85.9t0.166.
参考文献
| [1] | 牧正志 .さらに强ぃ鋼のための超微細粒鋼創製の新しぃメタラジ-とその将來の展望[J].金属(日本),2001,71(08):59-68. |
| [2] | S.TAGASHIRA;K. SAKAI .Deformation Microstructure and Tensile Strength of Cold Rolled Pearlitic Steel Sheets[J].ISIJ International,2000(11):1149-1155. |
| [3] | Maki T .Microstructure and tensile property of ultra-fine ferrite + cementite structure in high carbon steels[J].CAMP-ISIJ,2001,14:550-551. |
| [4] | M. Umemoto;Z.G. Liu;K. Masuyama .NANOSTRUCTURED Fe-C ALLOYS PRODUCED BY BALL MILLING[J].Scripta materialia,2001(8-9):1741-1745. |
| [5] | Sakuma T;Watanabe N;Nishizawa T .Effect of alloying element on the coarsening behavior of cementite particles in ferrite[J].Transactions of the Japan Institute of Materials,1980,21(03):159-168. |
| [6] | Wantang FU;T. FURUHARA;T. MAKI .Effect of Mn and Si Addition on Microstructure and Tensile Properties of Cold-rolled and Annealed Pearlite in Eutectoid Fe-C Alloys[J].ISIJ International,2004(1):171-178. |
| [7] | 孙淑华,张振戎,熊毅,吕知清,厉勇,傅万堂,牧正志.锰和硅添加对重度冷轧及退火后珠光体钢力学性能的影响[J].机械工程学报,2005(05):147-153. |
| [8] | 孙淑华,熊毅,傅万堂,邢广忠,古原忠,牧正志.共析珠光体钢在冷轧过程中的组织变化[J].金属学报,2005(03):267-270. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%