利用微弧氧化的方法在γ-TiAl合金上制备陶瓷膜,探讨了氧化过程中电流密度与成膜速度的关系.利用扫描电镜研究了氧化膜的表面形态和截面结构,结果表明,氧化膜由三层组成,且氧化膜与基体间有良好的冶金结合;物相分析发现氧化膜中含有金红石、Al2 TiO5和SiO2非晶成分,并且物相组成和分布与成膜时间及膜的深度无关;氧化膜的硬度随着氧化时间的增加而增加,极大值出现在距离膜基交界面约10μm附近的氧化膜中.1100℃下的高温氧化实验发现微弧氧化处理后样品的氧化速度只有原始基体材料的1/3,微弧氧化处理后提高了TiAl合金的抗氧化性.
参考文献
| [1] | 李成功;傅恒志;于翘.航空航天材料[M].北京:国防工业出版社,2002:84. |
| [2] | Diaz P;Ralph R;Edirisinghe M J .Transmission electron microscope characterization of a plasma-sprayed ZrO2-Y2O3-TiO2 thermal barrier coating[J].Materials Characterization,1998,41:55-67. |
| [3] | 邵德春.激光表面合金化提高钛合金高温抗氧化性能的研究[J].中国激光,1997(03):281. |
| [4] | 唐兆麟,王福会,吴维(山又).涂层对TiAl金属间化合物抗循环氧化性能的影响[J].中国有色金属学报,1998(01):56-60. |
| [5] | 刘道新,陈华,何家文.等离子渗氮与喷丸强化复合改进钛合金抗微动损伤性能[J].材料热处理学报,2001(03):49-54. |
| [6] | Kaestner P.;Rie KT.;Olfe J. .Plasma-assisted boriding of pure titanium and TiAl6V4[J].Surface & Coatings Technology,2001(0):248-252. |
| [7] | Yrokhin A L;Lyubimov V V;Ashitkov R V .Phase formation in ceramic coatings during plasma electrolytic oxidation of aluminum alloys[J].Ceramics International,1998,24(01):1-6. |
| [8] | Nie X;Leyland A;Song H W et al.Thickness effects on the mechanical properties of micro-arc discharge oxide coatings on aluminum alloys[J].Surface and Coatings Technology,1999,116:1955-1060. |
| [9] | Wenbin Xue;Zhiwei Deng;Ruyi Chen;Tonghe Zhang .Growth regularity of ceramic coatings formed by microarc oxidation on Al-Cu-Mg alloy[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2000(1/2):114-117. |
| [10] | Xue W;Wang C;Chen R et al.Structure and properties characterization of ceramic coatings produced on Ti-6Al-V alloy by microarc oxidation in aluminate solution[J].Materials Letters,2002,52:435-441. |
| [11] | Verdier S;Boinet M;Maximovitch S;Dalard F .Formation,structure and composition of anodic films on AM60 magnesium alloy obtained by DC plasma anodizing[J].Corrosion Science,2005,47:1429-1444. |
| [12] | 唐兆麟;王福会;吴维(山又) .微弧氧化处理对TiAl合金抗氧化性的影响[J].中国有色金属学报,1999,9(z1):63-68. |
| [13] | 薛文斌,王超,陈如意,李永良.ZL101铸造铝合金微弧氧化陶瓷层的组织和性能[J].材料热处理学报,2003(02):20-23. |
| [14] | 莫畏;邓国铢;罗方承.钛冶金[M].北京:冶金工业出版社,2002 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%