为探索提高工程机械易损零部件服役寿命的新技术,采用等离子熔覆工艺,以Ni-Cr-C混合合金粉末为添加材料,在易损零部件用钢Q235表面形成了以初生块状金属陶瓷Cr7C3为硬质耐磨相,以强韧性良好的γ/Cr7C3共晶为基体的复合材料冶金涂层,分析了涂层的显微组织和硬度,在室温干滑动磨损条件下测试了其耐磨性.研究结果表明:涂层组织致密,硬度较高,与基体之间为完全的冶金结合,在干滑动磨损条件下具有良好的耐磨性.
参考文献
| [1] | Zhao C.;Tian F.;Peng HR.;Hou JY. .Non-transferred arc plasma cladding of Stellite Ni60 alloy on steel[J].Surface & Coatings Technology,2002(1):80-84. |
| [2] | L. Shepeleva;B. Medres;W. D. Kaplan;M. Bamberger;A. Weisheit .Laser cladding of turbine blades[J].Surface & Coatings Technology,2000(1/3):45-48. |
| [3] | 张丽民,孙冬柏,李惠琪,刘邦武,樊自栓.等离子束表面冶金技术研究及其进展[J].金属热处理,2006(02):12-16. |
| [4] | Zhang DW.;Li FJ.;Lei TC. .Laser cladding of stainless steel with Ni-Cr3C2 for improved wear performance[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(2):1372-1376. |
| [5] | ZHANG Da-wei;Lei T C .The microstructure and erosive-corrosive wear performance of laser clad Ni-Cr3C2 composite coating[J].Wear,2003,255:129-133. |
| [6] | Zhang DW;Zhang XP .Laser cladding of stainless steel with Ni-Cr3C2 and Ni-WC for improving erosive-corrosive wear performance[J].Surface & Coatings Technology,2005(2/3):212-217. |
| [7] | Oliverira A S C M d';Vilar R;Feder C G .High temperature behavior of plasma transferred arc and laser Co-based alloy coatings[J].Applied Surface Science,2002,201:154-160. |
| [8] | LIU Yuan-fu,HAN Jian-min,Zhang Gu-Ling,Wang Jiu-Li,LI Min,YANG Wu-Bao,Liu Chi-Zi,LI Hui-qi,Yang Si-Ze.Microstructure and Wear Resistance of Plasma Jet Clad Ti5Si3/NiTi Composite Coating[J].中国物理快报（英文版）,2004(07):1314-1316. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%