选用齿科烤瓷用NiCr合金和支架用CoCr合金,利用脉冲Nd-YAG激光,在不同电压下进行焊接,考察焊件力学性能,优选电压条件,研究此条件下焊件熔焊区及其附近区域化学成分、显微组织变化规律.结果表明,适合齿科临床应用焊接电压为280V,此条件下可以得到显微组织致密、细小的熔焊区,熔焊区与两侧母材呈冶金结合,主要成分为Ni元素,以固溶体和化合物形式存在;Co、Cr元素部分溶入固溶体,部分与Mo、Be形成化合物.焊接中冶金过程充分,无新相生成.双向侧吹氩气可以对熔焊区起到良好的保护作用,无氧化物形成.
参考文献
| [1] | Watanabe I;Liu J;Atsuta M .Effect of welding method on joint strength of laser-welded gold alloy[J].American Journal of Dentistry,2003,16:231-234. |
| [2] | Toggya T;Shinosaki T .Introduction to laser welding in dentistry[J].Quint Dent Tech,1999,24(06):42-51. |
| [3] | Watanabe I;Liu J;Miura E .Penetration depth of cast titanium and gold alloy by laser[J].Journal of Dental Research,2000,79:187. |
| [4] | Baba N;Liu W J;Atsuta M .Mechanical strength of laser-welded cobalt-chromium alloy[J].J Biomed Mater Res Part B:Appl Biomater,2004,69B:121-124. |
| [5] | Liu J;Watanabe I;Yoshida K .Joint strength of laser-welded titanium[J].Dental Materials,2002,18:143-148. |
| [6] | Ikuya Watanabe;Jie Liu;Naoki Baba;Mitsuru Atsuta;Toru Okabe .Optimizing mechanical properties of laser-welded gold alloy through heat treatment[J].Dental materials,2004(7):630-634. |
| [7] | Longoni S;Sartori M;Davide R .A simplified method to reduce prosthetic misfit for a screw-retained, implant-supported complete denture using a luting technique and laser welding.[J].The Journal of Prosthetic Dentistry,2004(6):595-598. |
| [8] | Mai T A .Characterization of dissimilar joints in laser welding of steel-kovar,copper-steel and copper-aluminiu[J].Materials Science and Engineering A-structural Materials Properties Microstructure and Processing,2004,374:224-233. |
| [9] | 陈治清.口腔材料学[M].北京:人民医学出版社,2003 |
| [10] | Mackwood AP;Crafer RC .Thermal modelling of laser welding and related processes: a literature review[J].Optics & Laser Technology,2005(2):99-115. |
| [11] | 姜志清,赵铱民,郭天文,林丽红.激光焊接铁铬钼合金与钴铬合金的机械性能[J].口腔颌面修复学杂志,2003(02):124-127. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%