以Al-10wt%SiO2粉末为研究体系,对比机械混合与球磨的粉末,研究了球磨粉末的相组成和微结构,用差热分析的方法确定了两种粉末体系中的置换反应发生的温度,以此为据,优化了烧结两种粉末压坯的工艺.结果表明,4h球磨的粉末颗粒明显细化,部分SiO2颗粒嵌入Al基体,形成反应扩散耦Al/SiO2;混合粉末中置换反应不能发生,球磨粉末中置换反应的温度区间为560-680℃;球磨粉末的压坯在640℃烧结2h,可形成组织均匀的微米级Al2O3颗粒强化Al基复合材料.
参考文献
[1] | Jianghong Gong;Hezhuo Miao;Zhe Zhao .Effect of TiC-particle size on sliding wear of TiC particulate reinforced alumina composites[J].Materials Letters,2002(4/5):258-261. |
[2] | Yanfeng Han;Xiangfa Liu;Xiufang Bian .In situ TiB_2 particulate reinforced near eutectic Al-Si alloy composites[J].Composites, Part A. Applied science and manufacturing,2002(3):439-444. |
[3] | Ma Z Y;Ning X G;Lu Y X et al.In-situ Al4C3 dispersoid and SiC particulate mixture-reinforced aluminum composite[J].Scripta Metallurgica et Materialia,1994,31(02):131-135. |
[4] | Xiufang Wang;Gaohui Wu;Dongli Sun .Micro-yield property of sub-micron Al_2O_3 particle reinforced 2024 aluminum matrix composite[J].Materials Letters,2004(3/4):333-336. |
[5] | Hanabe M R;Aswath P B .Al2O3/Al particle-reinforced aluminum matrix composite by displacement reaction[J].Journal of Materials Research,1996,11(06):1562-1569. |
[6] | Breslin MC.;Xu L.;Fuller M.;Seeger J.;Daehn GS.;Otani T.;Fraser HL.;Ringnalda J. .PROCESSING, MICROSTRUCTURE, AND PROPERTIES OF CO-CONTINUOUS ALUMINA-ALUMINUM COMPOSITES[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1995(1/2):113-119. |
[7] | Tjong SC.;Ma ZY. .Microstructural and mechanical characteristics of in situ metal matrix composites [Review][J].Materials Science & Engineering, R. Reports: A Review Journal,2000(3/4):49-113. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%