用Geeble1500热模拟实验机模拟不同始轧温度、冷却强度以及变形量和应变速率下AZ31合金的铸轧行为.结果显示:AZ31镁合金铸轧组织对应变速率和变形量均具有较强的敏感性.当ε由0.005s-1增到0.1s-1时,铸轧组织的晶粒逐渐变小,同时晶界析出物减少.变形量ε由20%增加到50%时,晶粒组织细化明显.试验得出了AZ31镁合金连续铸轧工艺的边界工艺条件,在此条件下,获得铸轧板的力学性能如下:70 HV0.5,σb为210-240 MPa,σ0.2为180-200MPa,δ为3%-6%.
参考文献
| [1] | Cahn R W;师昌绪;柯俊.非铁合金的结构性能[M].北京:科学出版社,1999 |
| [2] | Mordike B L;Ebert T .Magnesium properties-applications-potential[J].Materials Science and Engineering A-structural Materials Properties Microstructure and Processing,2001,302:37-45. |
| [3] | R.E.Brown .Australian Magnesium Projects-Update[J].Light Metal Age,2000(3/4):54-57. |
| [4] | Su-Hai Hsiang;Jer-Liang Kuo .An investigation on the hot extrusion process of magnesium alloy sheet[J].Journal of Materials Processing Technology,2003(1/3):6-12. |
| [5] | Mordike B L .Magnesium and magnesium alloys[J].Journal of Japan Institute of Light Metals,2001,51(01):2-13. |
| [6] | 余琨,黎文献,王日初,马正青.变形镁合金的研究、开发及应用[J].中国有色金属学报,2003(02):277-288. |
| [7] | Kojima Y.; .Platform Science and Technology for Advanced Magnesium Alloys[J].Materials Science Forum,2000(0):3-18. |
| [8] | 周海涛,马春江,曾小勤,丁文江.变形镁合金材料的研究进展[J].材料导报,2003(11):16-18,55. |
| [9] | 王渠东,丁文江.镁合金及其成形技术的国内外动态与发展[J].世界科技研究与发展,2004(03):39-46. |
| [10] | 林暾熹.双辊快速连续铸轧超薄带坯技术进展[J].轻合金加工技术,2001(10):14-16. |
| [11] | 王祝堂.迈向新世纪的世界铝带坯铸轧[J].轻合金加工技术,2001(04):8-15. |
| [12] | Takatani M;Gandin Ch-A;Rappaz M .Ebsd characterization and modeling of columnar dendritic grains growing in the presence of fluid flow[J].Acta Metalluraica,2000,48(03):675-688. |
| [13] | Sung S. Park;Jung G. Lee;Young S. Park .Fabrication of Mg Alloy Strips by Strip Casting[J].Materials Science Forum,2003(Pt.2):599-604. |
| [14] | 李铮,赵凯,邸洪双,王国栋.双辊铸轧法生产变形镁合金薄带新工艺的研究[J].轻金属,2003(12):35-37. |
| [15] | D. Liang;C. B. Cowley .The Twin-Roll Strip Casting of Magnesium[J].JOM,2004(5):26-28. |
| [16] | 黄伯云;李成功;石力开.中国材料工程大典[M].北京:化学工业出版社,2006 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%