采用机械合金化法制备了Cu-0.5wt％Nb纳米弥散强化铜合金。通过金相、透射电镜观察了该合金粉末态、冷轧态及不同温度退火后合金的组织结构变化。通过测量该合金不同状态的硬度及相对电导率,实验结果表明,其冷轧态硬度较高(可达160kg/mm2),随退火温度升高硬度呈缓慢下降趋势;900℃退火后,硬度仍可达91kg/mm2,表明此合金抗高温软化性能较好.此外该合金相对电导率最高可达89% IACS,这进一步说明利用机械合金化法制备的Cu-0.5wt%Nb合金具有优越的综合性能.
参考文献
| [1] | Teruo Takahashi;Yasuhiko Hashimoto .Preparation of dispersion-strengthened coppers with NbC and TaC by mechanical alloying[J].Materials Transactions-Japan Institute of Metals,1991,32(04):389-397. |
| [2] | E. Botcharova;M. Heilmaier;J. Freudenberger .Supersaturated solid solution of niobium in copper by mechanical alloying[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2003(1/2):119-125. |
| [3] | 周农,唐晖,周廉.铜-铌复合体冷加工后抗拉强度和导电性能的研究[J].稀有金属材料与工程,1994(02):47-52. |
| [4] | J.H.Chung;J.S.Song;S.I.Hong .Bundling and drawing processing of Cu-Nb microcomposites with various Nb contents[J].Journal of Materials Processing Technology,2001(1/3):604-609. |
| [5] | Freudenberger J;Botcharova E;Schultz L .Formation of the microstructure in Cu-Nb alloys[J].Journal of Materials Science,2004(16/17):5343-5345. |
| [6] | Botcharova E;Freudenberger J;Schultz L .Cu-Nb alloys prepared by mechanical alloying and subsequent heatment[J].Journal of Alloys and Compounds,2004,365:157-163. |
| [7] | Benghalem A;Morris D G .Microstructure and mechanical properties of concentrated copper-niobium alloys prepared by mechanical alloying[J].Materials Science and Engineering,1993,A161:255-266. |
| [8] | Morris M A;Morris D G .Microstructural refinement and associated strength of copper alloys obtained by mechanical alloying[J].Materials Science and Engineering A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,1989,AⅢ:115-127. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%