研究了余热热处理工艺对Al-Si-Cu合金中Cu元素的固溶效果、共晶Si颗粒形貌及尺寸变化、以及该工艺对合金铸件力学性能的影响.结果表明,余热热处理工艺条件下,铸件可以在更短的时间内获得理想的固溶效果.通过分析铸件微观组织显微可知,余热热处理工艺可以通过缩短固溶处理时间有效地抑制共晶Si颗粒的粗化,在4h的固溶处理中Si颗粒平均尺寸持续减小且未出现粗化趋势.采用相同工艺参数,余热热处理工艺条件下制备的单铸试棒抗拉强度比传统T6热处理工艺提升约15%.
参考文献
| [1] | Davis J R.ASM specialty handbook:aluminum and aluminum alloys[M].American Society for Metals Park,OH,USA,1993 |
| [2] | A.M. SAMUEL;J. GAUTHIER .Microstructural Aspects of the Dissolution and Melting of Al_2Cu Phase in Al-Si Alloys during Solution Heat Treatment[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1996(7):1785-1798. |
| [3] | Brooks C R.Heat treatment,structure and properties of nonferrous alloys[M].American Society for Metals Park,OH,USA,1982 |
| [4] | L. HE;J. KANG;T. HUANG .The Integrated Technique for the Heat Treatment of Aluminium-alloy Castings: a Review[J].Heat Treatment of Metals,2004(3):69-72. |
| [5] | 黄新民.变质和热处理工艺对铸造铝硅铜合金组织性能的影响[J].热加工工艺,1999(05):40. |
| [6] | 黄丽雅,钱翰城,沈玲,张钊,王真见.铸造铝硅合金AlSi7Cu2Mg的T7热处理工艺[J].铸造技术,2004(02):108-109. |
| [7] | 任勤.ADC12铝硅合金铸件热处理工艺的改进[J].金属热处理,1997(01):47-49. |
| [8] | 吴其清.铝合金的熔炼工业生产过程与工艺技术[J].冶金丛刊,2004(06):5-6,50. |
| [9] | 孙继陶.铝合金铸件中气孔的形成机理及防止方法[J].甘肃冶金,2004(04):35-36,40. |
| [10] | 戚正风.固态技术中的扩散与相变[M].北京:机械工业出版社,1998 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%