在试验室模拟薄板坯连铸连轧过程,板坯均热后被轧制到7mm厚并通过控冷来模拟辊道冷却和带钢的缓慢卷取过程.本文选用低碳钢,研究了V、N、Nb微合金化对其组织和性能的影响.通过试验证明在V-N钢中加入Nb对钢的强化机制有较大影响,使V-N-Nb钢中的析出强化增大,这表明V-N-Nb微合金化可充分地发挥微合金元素在钢中的析出强化作用,析出强化对屈服强度的贡献比V-N微合金化提高17MPa.
参考文献
[1] | P J Lubensky;S L Wigman;D J Johnson.High Strength Steel Produced Via Direct charging Using Thin Slab Technology[A].ISS,Pittsburgh PA,1995:225-233. |
[2] | M Korchynsky;S Zajac.Flat Rolled Products from Thin-Slab Technology-Technological and Economic Potential,Thermo-Mechanical Processing[A].Stockholm,Sweden,1996:364-381. |
[3] | WANG Zhaifang .Strenthening of V-beating Microalloyed Steel in Hot Rolling and Accelerated Cooling[J].Iron & Steel,1996,31(11):39-43. |
[4] | Medina S F;Lopez V .Static Recrystallization in Austinite and Its Influence on Microstructural Changes in C-Mn Steel and Vanaduim Microalloyed Steel at the Hot Strip Mill[J].Isij International,1993,32:605. |
[5] | ZHANG Juan;YANG Caifu;ZHANG Yongqnan.The Effect of Composition on The Propertoes of Vanadium Containing Strip Rolled from Thin Slab[A].,2004 |
[6] | 雍歧龙;马鸣图;吴宝榕.微合金钢-物理和力学冶金[M].北京:机械工业出版社,1989:26-59. |
[7] | 于浩,康永林,王克鲁,柳得橹,傅杰.CSP低碳钢薄板连铸坯的连续冷却转变及显微组织细化[J].钢铁研究学报,2002(01):42-46. |
[8] | Y. LI;D. N. CROWTHER;R. S. MITCHELL .The Evolution of Microstructure during Thin Slab Direct Rolling Processing in Vanadium Microalloyed Steels[J].ISIJ International,2002(6):636-644. |