在铝合金LY12表面激光表面熔覆原位自生TiB颗粒增强耐磨涂层.采用SEM、TEM和XRD对涂层的显微组织和物相组成进行观察分析.激光熔覆Al-Ti-Fe-B复合涂层相组成为α-Al,Tib,Al3Ti以及Al3Fe.熔覆涂层的显微硬度随着涂层中TiB含量的增加而明显增加,涂层最高硬度可达900HV0.2.磨损试验结果显示,熔覆涂层的磨损失重随TiB含量的增加而减少.通过对试样的磨损形貌观察,对比分析了涂层与基体铝合金的磨损机理.
参考文献
| [1] | 纪红,许越,吕祖舜,周德瑞.铝合金激光表面强化的研究进展[J].材料科学与工艺,2003(02):220-224. |
| [2] | Yang Y. .Microstructure and properties of laser-clad high-temperature wear-resistant alloys[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,1999(1/2):19-23. |
| [3] | L. Shepeleva;B. Medres;W. D. Kaplan;M. Bamberger;A. Weisheit .Laser cladding of turbine blades[J].Surface & Coatings Technology,2000(1/3):45-48. |
| [4] | 丁健君,郑恢俊.AA6061铝基材上激光熔覆Cu/Cr合金层的研[J].激光杂志,2001(02):57-59. |
| [5] | 王冬涛,李会山,王惠滨.铝合金表面激光熔覆SiC颗粒增强复合耐磨涂层研究[J].汽车工艺与材料,2006(04):7-10. |
| [6] | Ming Q.;Chen ZD.;Lim LC. .Laser cladding of nickel-based hardfacing alloys[J].Surface & Coatings Technology,1998(2/3):174-182. |
| [7] | M. Bamberger .Laser surface hardening of structural ferrous alloys[J].International Materials Reviews,1998(5):189-203. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%