采用非平衡闭合场磁控溅射方法在Cr12MoV冷作模具钢表面制备CrTiAlN单一涂层和CrTiAlN/MoST复合涂层,通过AFM、XRD、显微硬度、划痕和磨损试验综合分析涂层相结构和的表面性能.实验结果表明,CrTiAlN/MoST复合涂层比CrTiAlN单一涂层更光滑、致密,(Cr,Ti,Al)N在(111)晶面呈强烈的衍射峰,无明显的MoS2衍射峰.Crl2MoV经PVD处理后,表面显微硬度和耐磨性得到了明显的提高,尤其是复合涂层,由于CrTiAlN硬涂层抗磨和MoST软涂层减摩的综合作用表现出比CrTiAlN涂层更低的磨损率,主要的磨损机制为逐层剥落的疲劳磨损.
参考文献
| [1] | P. J. Kelly;R. D. Arnell .Magnetron sputtering: a review of recent developments and applications[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2000(3):159-172. |
| [2] | Chou Wen-Jun.Mechanical properties of TiN thin film coaings on 304 stainless steel substrates[J].Surface and Coatings Techonology,2002(149):7-13. |
| [3] | Ezugwu E O;Okeke C I.Tool life and wear mechanisms of TiN coated tools in an intermittent catting operation[J].Journal of Materials Processing Technology,2001(116):10-15. |
| [4] | S. G. Harris;E. D. Doyle;A. C. Vlasveld;J. Audy;J. M. Long;D. Quick .Influence of chromium content on the dry machining performance of cathodic arc evaporated TiAlN coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(1/2):185-194. |
| [5] | Harris S G.A study of the wear mechanisms of Til-xAlxN and Ti1-x-yAlx CryN coated high-speed steel twist drills under dry machining conditions[J].Wear,2003(254):723-734. |
| [6] | Wu S K.An investigation of unbelanced-magnetron sputterd TiAlN films on SKH51 high-speed steel[J].Surface and Coatings Techonology,2000(124):97-103. |
| [7] | Shicai Yang,Eric Wiemann,D.G. Teer.Applications of Cr-Based Metal Nitride Hard Coatings Using Multi-Magnetron Sputtering Sources and Elemental Metal Targets[J].材料热处理学报,2004(05):821-826. |
| [8] | ZHANG Guo-jun,YANG Shi-cai,JIANG Bai-ling,BAI Li-jing,CHEN Di-chun,WEN Xiao-bin,TEER D.G.Up-scaled Teer-UDP850/4 Unbalanced Magnetron Deposition System Used for Mass-Production of CrTiAlN Hard Coatings[J].材料热处理学报,2004(05):827-831. |
| [9] | Guizhen Xu;Zhongrong Zhou;Jiajun Liu;Xiaohua Ma .An investigation of fretting behavior of ion-plated TiN, magnetron-sputtered MoS{sub}2 and their composite coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(1):46-52. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%